[ 0040 ] fig1 shows diagrammatically an apparatus for producing a tubular film which comprises an extrusion part of ring die 1 and spinning vat 4 , a wash section 25 , 26 , a plasticizer vat 27 , a dryer 28 and conditioner 29 as essential constituents . the extrusion part is described in detail with reference to fig2 . the tubular film 9 passed out of the spinning vat 4 passes through the wash section 25 , 26 which consists of two or more wash vats having a plurality of guide rolls per wash vat . for example , five wash vats having from seven to nine guide rolls per wash vat can be provided . the wash water is introduced into the last wash vat in counter current to remove the last nmmo residues from the surface of the tubular film 9 . the nmmo content is kept at from 12 to 16 % by weight at the exit of the first wash vat . within the wash section the temperature increases from vat to vat and is from about 60 ° c . to about 70 ° c . in the last wash vat . after the wash section the tubular film is passed through the plasticizer vat 27 which contains a from about 5 % to 15 % strength by weight aqueous glycerol solution heated to from about 50 ° c . to 65 ° c . above the wash section 25 , 26 and the plasticizer vat 27 extends an extractor 33 for the water vapor ascending from the vats . after the tubular film 9 leaves the plasticizer vat 27 , it is introduced via guide rolls 31 and through a pinch - roll pair 32 into a dryer 28 . this has one or more drying zones , for example four zones , which have different temperatures . in the entrance zone of the dryer 28 a temperature of 120 ° c ., for example , prevails , which falls toward the exit zone , so that in this a temperature of 80 ° c . prevails . in the conditioner 29 , the tubular film 9 is then moistened to a water content of from about 8 % to about 24 % by weight , based on the total weight of the tube , and is then wound up to form a roll 30 . by means of a driven roll 31 situated above the spinning vat , the tubular film is transported into the wash section . for the purposes of the present invention , owing to the low mechanical load - bearing capacity of the thin - walled tubular films in the wet state , the use of particularly gentle technical measures is required when conveying the material through the spinning , washing and after treatment . for this it is necessary to configure all guide rolls to be separately controllable in very fine stages , and to support the transport , if appropriate , further via conveyor belts or hydraulic support tubes . the tubular film is freed from any residual nmmo present in the course of the wash section at differing temperatures , first with aqueous nmmo solutions ( wash section 25 , addition of microbicide ), and finally with fresh water ( wash section 26 ). the counter current flow rates , concentrations and temperatures of the wash baths have a significant effect on the efficiency of washing . the cleaning performance is improved by additionally sprinkling the tubular films on the paths which do not dip into the baths . for the elimination of very small residual amounts , an ultrasound treatment in the last section of the wash section ( wash section 26 ) under appropriate conditions and addition of surfactants and an increase of the ph is particularly effective . if appropriate , brightening by oxidizing substances is possible . the tubular film is then treated with plasticizers , preferably with glycerol in aqueous solution which , if appropriate , further contains preservatives . the tubular film leaves the wet part of the plant in the laid - flat state . the liquid still then bound in the tubular film because of swelling must then be removed by the action of heat . this can only take place under highly specific mild conditions in order not to damage the tubular material and to give the product , in a highly targeted manner , the profile of properties with regard to strength and elongation required for later application . this takes place in the dryer 28 , a hot - air dryer having a temperature zone subdivided into up to a plurality of temperature zones , in which , at a high air velocity , the water diffusing to the film surface is removed . by maintaining a defined internal pressure in the tubular film and a constant tension in the longitudinal direction , the mechanical properties necessary for later application can be imparted to the material in a targeted manner . the water content of the material at the dryer end is of essential importance for the following processing . for this purpose , the tubular film can be dried in the dryer either to from about 14 % to 24 % moisture , preferably from about 16 % to 18 %, or can be set to about from about 8 % to about 10 % residual moisture and then remoistened to from about 16 % to about 18 %. the latter can be effected by passing the tubular film through the conditioner 29 , a chamber having defined temperature / moisture conditions , by spraying with finely atomized water or the like . suitable processes are known from the literature . [ 0054 ] fig2 shows a diagrammatic view of the extrusion part of the apparatus according to the invention . this comprises , for extruding an aqueous cellulose / nmmo solution having dissolved and suspended additives to form a tubular film , a ring die 1 and a spinning vat 4 which is filled with a spinning or precipitation bath 3 . the spinning bath 3 comprises an aqueous nmmo solution having an nmmo content of from about 5 % to about 50 % by weight , in particular from about 15 % to about 35 % by weight . the spinning solution is introduced into the ring die 1 which is known per se through a heated jacketed pipe using a spinning pump which is not shown . the ring die 1 has a jacket for heating the spinning solution by means of a heating medium 21 . the temperature of the ring die 1 can be from about 70 ° c . to about 120 ° c . the tubular film is drawn in the longitudinal direction in an air section 2 in such a manner that the take - off speed of the tubular film is chosen to be greater than the exit velocity of the spinning solution . the quotient of take - off speed and exit speed gives the longitudinal stretching . the tubular film 8 extruded from the die gap 19 passes through this outer air section 2 between die exit and spinning bath surface , the cross section being able to be increased by blowing , or decreased by shrinking . the take - off ratio is in the range from about 0 . 6 to about 5 , preferably in the range from about 0 . 8 to about 2 . 0 . if appropriate , additional heating can be performed by blowing with a gaseous medium . transverse stretching is achieved primarily by the supporting air pressure present in the tubular film which is higher than the external atmospheric pressure and / or , secondly , by the hydrostatic pressure of the inner bath , the surface 22 of which projects above the outer bath level . if appropriate , for the transverse stretching , a spreader tube can also be used . the ring die 1 comprises a predistributor disc 5 , an adjusting device 6 , a side - fed die 7 having a central passage 18 and the die gap 19 . the predistributor disc 5 causes uniform feed over the periphery of the spinning solution into the die gap 19 . the die gap 19 is a ring gap having a width of from about 0 . 1 mm to about 3 mm , preferably from about 0 . 2 mm to 1 . 5 mm . the diameter of the die gap is greater than the outer diameter of a tube 12 . the tubular film thickness is finely adjusted using the adjusting device 6 of the side - fed die 7 . the tube 12 encloses a feed tube and an extraction tube 10 and 11 , respectively , for the inner precipitation bath 13 which is charged into the tubular film and forms a gap 17 with the outlet 18 . this inner precipitation bath 13 likewise comprises an aqueous nmmo solution having an nmmo content of from about 1 % to about 50 % by weight , in particular from about 15 % to 35 % by weight . the tubular film 16 passes over the guide roll 15 , a driven guide roll along a contact section 20 in a fold - free and crease - free manner and without constriction . there is no risk of forming creases and folds on the guide roll . the tubular film 16 , which , as described , is transversely stretched and conducted perpendicularly , is passed out of the spinning bath upward at an incline within the spinning bath 3 after the guide roll 15 perpendicularly or at an angle of from about 10 ° to about 80 ° to the horizontal . the tubular film 14 running upward at an incline is pinched together by the internal pressure of the spinning bath , just below the surface of the spinning bath , and is conducted out of the spinning bath 3 in the laid - flat state . scrapers 24 on both sides of the tubular film 14 , which is folded up , hold back the excess spinning bath solution . the width of the laid - flat tubular film 9 after being scraped off near the exit of the spinning vat 4 is used as a control parameter for the height of the inner bath column and / or of the air pressure in the tubular film interior ( inner air gap ). any deviation in width of the laid - flat tubular film 9 from a preset value causes a readjustment of the inner column and / or the air pressure in the tubular film interior . the example which follows serves for a more detailed explanation of the invention . percentages therein are percentages by weight unless stated otherwise . 7 . 45 kg of ground wood pulp ( sulfite pulp modo dissolving , from modo ) having a mean degree of polymerization dp of 800 , determined by the cuoxam method , were slurried together with 10 kg of finely ground wheat bran and 3 . 3 kg of commercially conventional corn protein ( zein ) in 130 kg of a 60 % strength nmmo solution . adding naoh set a ph of 11 . in addition , 20 g of propyl gallate were added as stabilizer . with heating and stirring , h 2 o was then distilled off under reduced pressure at 25 mbar with increasing temperature until the nmmo concentration was 87 %, based on the total weight of solvent ( equivalent to nmmo monohydrate ). the spinning solution thus prepared was extruded at a temperature of 75 ° c . through a ring gap die having a gap diameter of 20 mm and a gap width of 0 . 5 mm . at a speed of 20 m / min , the tubular film first passed through an air section of 10 cm . a continuously renewed inner precipitation bath having a 15 % strength nmmo solution which had been cooled to 5 ° c . was introduced into the tubular film interior . then the tubular film passed through a precipitation bath section of 10 m , in which it was turned round at half the distance . the spinning bath contained a solution of the same composition , concentration and temperature as the inner precipitation bath . the flat width after leaving the spinning vat was 35 mm . the tubular film then passed through four wash vats . at the end of the last vat , water was introduced which conducted in counter current . at the exit of the first vat , the nmmo content was kept in this manner at from 12 to 16 %. the temperature rose to from 60 to 70 ° c . in the last vat . finally , the tubular film was conducted through a plasticizer vat which contained a 10 % strength glycerol solution at a temperature of 60 ° c . the flat width on leaving the plasticizer vat was still 28 mm . the tubular film was then dried in the inflated state using hot air between two pinch rolls . the dryer had a plurality of zones of decreasing temperature . the zone at the inlet had a temperature of 120 ° c ., and that at the outlet 80 ° c . the tubular film was then moistened until its water content was from 14 to 18 % ( based on the weight of the cellulose ). the bursting pressure of the tubular film was 14 kpa . the tubular film was shirred to form shirred sticks by one of the known processes . the shirred sticks were stuffed with sausage meat emulsion using an automatic stuffing machine ( frankamatic ®), scalded and smoked . the sausages could then be bitten , chewed and swallowed without problems .
a seamless cellulose - based tubular film is produced by extruding an aqueous n - methylmorpholine n - oxide spinning solution through a ring die . the tubular film comprises at least one protein , at least one filler and , if appropriate , a stabilizer . the tubular film passes through a spinning bath 3 in which it is turned around and , after its exit from the spinning bath it passes through a wash device 25 , 26 , a plasticizing device 27 and a dryer 28 .