examples of the present invention are described with reference to table 1 . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 18 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 5 mass % hydrogenated rosin ester ( trade name “ pinecrystal ke - 311 ”, produced by arakawa chemical industries , ltd . ): 12 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 10 mass % 1 , 3 - butylene glycol ( produced by daicel chemical industries , ltd . ): 1 . 5 mass % oleic acid (“ purified oleic acid ”, produced by nof corporation ): 2 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 43 . 8 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 2 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , hydrogenated rosin ester , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the lidocaine , 1 , 3 - butylene glycol , and oleic acid , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 140 g / m 2 . a polyester woven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ). in this preparation , the proportion of lidocaine and dissolving agent was 1 : 0 . 5 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 15 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 10 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 20 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 48 . 3 mass % isostearic acid ( produced by kokyu alcohol kogyo co ., ltd . ): 1 . 5 mass % 1 , 3 - butylene glycol ( produced by daicel chemical industries , ltd . ): 1 . 5 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 2 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the isostearic acid , lidocaine , and 1 , 3 - butylene glycol , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 140 g / m 2 . a polyester woven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ). in this preparation , the proportion of lidocaine and dissolving agent was 1 : 1 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 18 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 10 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd .) : 20 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ) : 46 . 9 mass % isostearic acid ( produced by kokyu alcohol kogyo co ., ltd . ): 1 . 8 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 3 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the isostearic acid , lidocaine , and dipropylene glycol , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 140 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ) . in this preparation , the proportion of lidocaine and dissolving agent was 1 : 1 . 15 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k .) : 20 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ) : 8 mass % hydrogenated rosin ester ( trade name “ pinecrystal ke - 311 ”, produced by arakawa chemical industries , ltd . ): 20 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 48 . 2 mass % isostearic acid ( produced by kokyu alcohol kogyo co ., ltd . ): 1 . 5 mass % 1 , 3 - butylene glycol ( produced by daicel chemical industries , ltd . ): 1 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 3 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , hydrogenated rosin ester , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the isostearic acid , lidocaine , and 1 , 3 - butylene glycol , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 160 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ) . in this preparation , the proportion of lidocaine and dissolving agent was 1 : 5 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 18 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 5 mass % hydrogenated rosin ester ( trade name “ pinecrystal ke - 311 ”, produced by arakawa chemical industries , ltd . ): 12 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 10 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 38 . 1 mass % isostearic acid ( produced by kokyu alcohol kogyo co ., ltd . ): 2 . 1 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 3 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , hydrogenated rosin ester , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the isostearic acid , lidocaine , and dipropylene glycol , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 100 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ) . in this preparation , the proportion of lidocaine and dissolving agent was 1 : 1 . 3 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 20 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 8 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 20 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 49 . 165 mass % isostearic acid ( produced by kokyu alcohol kogyo co ., ltd . ): 1 . 4 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 2 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the isostearic acid , lidocaine , and dipropylene glycol , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 150 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ) . in this preparation , the proportion of lidocaine and dissolving agent was 1 : 2 . 05 by mass ratio . styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 20 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 5 mass % hydrogenated rosin ester ( trade name “ pinecrystal ke - 311 ”, produced by arakawa chemical industries , ltd . ): 15 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 5 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 48 . 2 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 3 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisoprene , hydrogenated rosin ester , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . a solution separately prepared by mixing the polysorbate 80 and lidocaine , followed by dissolution at 80 ° c ., was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 140 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ). styrene - isoprene - styrene block copolymer (“ kraton d1161 ”, produced by kraton jsr elastomers k . k . ): 15 mass % polyisobutylene ( trade name “ himol 6h ”, produced by jx nippon oil & amp ; energy corporation ): 10 mass % terpene resin ( trade name “ ys resin 1150n ”, produced by yasuhara chemical co ., ltd . ): 20 mass % liquid paraffin ( trade name “ hicall ”, produced by kaneda corporation ): 51 . 3 mass % light anhydrous silicic acid ( trade name “ sylysia 350 ”, produced by fuji silysia chemical ltd . ): 0 . 5 mass % dibutylhydroxytoluene ( trade name “ bht ”, produced by honshu chemical industry co ., ltd . ): 0 . 2 mass % the production method using these materials according to the above formulation was as follows . the styrene - isoprene - styrene block copolymer , polyisobutylene , terpene resin , light anhydrous silicic acid , dibutylhydroxytoluene , and liquid paraffin were placed in a dissolution mixer and dissolved under heating at 150 ° c . the lidocaine was added thereto , and the mixture was mixed under heating at 140 ° c . until the mixture became homogeneous , thereby obtaining a plaster solution . the plaster solution was applied to a polyester film treated with silicon so that the plaster weight was 140 g / m 2 . a polyester nonwoven fabric was pasted thereto and cooled . the resultant was then cut into a rectangle ( about 14 cm × 10 cm ). the preparations obtained in examples 1 to 6 and comparative examples 1 and 2 were subjected to the following tests . a ball tack adhesion test was performed according to the test method described in drug approval and licensing procedures in japan . as shown in table 2 , examples 1 to 6 ( hereinafter referred to the “ invention products ”) showed excellent adhesion . the adhesion of comparative example 1 was about half of those of the invention products . comparative example 2 had satisfactory adhesion , because no dissolving agent was used . as shown in fig1 , the preparations were attached to the human skin for 4 hours , 8 hours , and 12 hours . after each time period was passed , the preparations were removed . the amount of drug remaining in each preparation was measured to determine the drug remaining ratio on the premise that the amount of drug prior to attachment was 100 %. the drug remaining ratio after attachment for 12 hours was 96 to 99 % in the comparative examples , while the results of all of the invention products were 80 % or less , and the amount of drug released into the human skin was 20 % or more . the preparations were attached to the human skin for 12 hours and then removed . 4 hours , 8 hours , and 12 hours after the attachment of the preparations , and 24 hours after the removal of the preparations , the blood was extracted , and the level of lidocaine in the blood was measured . fig2 is a graph showing the results . the results reveal that the preparations comprising a dissolving agent composed of isostearic acid and dipropylene glycol showed generally good results .
non - aqueous patches comprising lidocaine , which is not dissolved and is present in a crystalline state , have poor permeability to the skin . therefore , non - aqueous patches have a high concentration of lidocaine . it is pointed out that lidocaine has an adverse effect on the heart . prolonged use of a high concentration of lidocaine causes side effects , such as shock , rubor , and irritating sensation . external preparations comprising more than 5 mass % of lidocaine are designated as powerful drugs , and cannot be used as household medicine . provided is a non - aqueous patch that is effective to relieve muscle pain , the non - aqueous patch comprising lidocaine and / or its reactant , and a dissolving agent composed of an organic acid and a polyalcohol , which are contained in a base .