the naturally degradable green flowerpot in this example is prepared by the following method , comprising : 1 ) crushing plant fiber and sieving it with a sieve of 60 - 100 mesh to obtain a sieved material , 2 ) fully mixing 60 grams of the above sieved material and 200 grams of adhesive agent solution which contains 20 % solid content in a mixer , and then removing to a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , 3 ) adding 1 gram of zinc stearate as lubricant and 5 - 10 grams of water into the above mixed material , and then stirred fully to obtain a molding material , 4 ) putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 50 - 100 mpa for 0 . 4 - 1 . 5 minutes , and conducting an exhaustion during pressing for 1 to 3 times to obtain a shaped product , and 5 ) polishing or burnishing the above shaped products to wipe off burr and drilling drainage hole ( s ) at its bottom , in which the adhesive agent solution in step 2 ) is prepared by adding 10 grams of polyvinyl alcohol ( pva ), 10 grams of polycaprolactone ( pcl ), 10 grams of amino - resin , and 10 grams of oxidized starch into water in 90 - 95 ° c . sequentially with fully stirring . the naturally degradable green flowerpot in this example is prepared by the following method , comprising : 1 ) crushing plant fiber and sieving it with a sieve of 60 - 100 mesh to obtain a sieved material , 2 ) mixing fully 80 grams of the above sieved material and 100 grams of adhesive agent solution which contains 20 % solid content in a mixer , and then removing to a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , 3 ) adding 1 gram of zinc stearate as lubricant and 5 - 10 grams of water into the above mixed material , and then stirred fully to obtain a molding material , 4 ) putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 50 - 100 mpa for 0 . 4 - 1 . 5 minutes , and conducting an exhaustion during pressing for 1 to 3 times to obtain a shaped product , and 5 ) polishing or burnishing the above shaped products to wipe off burr and drilling drainage hole ( s ) at its bottom , in which the adhesive agent solution in step 2 ) is prepared by adding 5 grams of polycaprolactone ( pcl ), 5 grams of amino - resin , and 10 grams of oxidized starch into water in 90 - 95 ° c . sequentially with fully stirring . the naturally degradable green flowerpot in this example is prepared by the following method , comprising : 1 ) crushing plant fiber and sieving it with a sieve of 60 - 100 mesh to obtain a sieved material , 2 ) mixing fully 70 grams of the above sieved material and 150 grams of adhesive agent solution which contains 20 % solid content in a mixer , and then removing to a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , 3 ) adding 1 gram of zinc stearate as lubricant and 5 - 10 grams of water into the above mixed material , and then stirred fully to obtain a molding material , 4 ) putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 50 - 100 mpa for 0 . 4 - 1 . 5 minutes , and conducting an exhaustion during pressing for 1 to 3 times to obtain a shaped product , and 5 ) polishing or burnishing the above shaped products to wipe off burr and drilling drainage hole ( s ) at its bottom , in which the adhesive agent solution in step 2 ) is prepared by adding 5 grams of polyvinyl alcohol ( pva ), 5 grams of amino - resin , and 20 grams of oxidized starch into water in 90 - 95 ° c . sequentially with fully stirring . the naturally degradable green flowerpot in this example is prepared by the following method , comprising : 1 ) crushing plant fiber and sieving it with a sieve of 60 - 100 mesh to obtain a sieved material , 2 ) mixing fully 60 grams of the above sieved material and 160 grams of adhesive agent solution which contains 25 % solid content in a mixer , and then removing to a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , 3 ) adding 1 gram of zinc stearate as lubricant and 5 - 10 grams of water into the above mixed material , and then stirred fully to obtain a molding material , 4 ) putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 50 - 100 mpa for 0 . 4 - 1 . 5 minutes , and conducting an exhaustion during pressing for 1 to 3 times to obtain a shaped product , and 5 ) polishing or burnishing the above shaped products to wipe off burr and drilling drainage hole ( s ) at its bottom , in which the adhesive agent solution in step 2 ) is prepared by adding 5 grams of polyvinyl alcohol ( pva ), 5 grams of polycaprolactone ( pcl ), 5 grams of amino - resin , and 25 grams of oxidized starch into water in 90 - 95 ° c . sequentially with fully stirring . this example is to prepare a naturally degradable green flowerpot for a 2 - month planting period with the following method , comprising the steps of : adding 3 grams of polyvinyl alcohol ( pva ), 2 grams of polycaprolactone ( pcl ), 2 grams of amino resin , and 18 grams of oxidized starch into 125 grams of water in 90 - 95 ° c . sequentially with fully stirring to obtain adhesive agent solution , adding 75 grams of rice husk powder in 80 mesh into the above adhesive agent solution , and stirring them fully in a mixer , and then removing into a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , adding 1 grams of zinc stearate and 6 grams of water in the above mixed material with fully stirring to obtain a molding material , and putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 70 mpa for 1 minute , and conducting an exhaustion for 2 times during pressing to obtain a shaped product . this example is to prepare a naturally degradable green flowerpot for a 6 - month planting period with the following method , comprising the steps of , adding 7 grams of polyvinyl alcohol ( pva ), 8 grams of amino resin , and 10 grams of oxidized starch into 125 grams of water in 90 - 95 ° c . sequentially with fully stirring to obtain adhesive agent solution , adding 75 grams of bamboo powder in 100 mesh into the above adhesive agent solution , and stirring them fully in a mixer , and then removing into a drying roller for dehydrating until the content of water is 5 %- 10 % to obtain a mixed material , adding 1 grams of zinc stearate and 6 grams of water in the above mixed material with fully stirring to obtain a molding material , and putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 70 mpa for 1 minute , and conducting an exhaustion for 2 times during pressing to obtain a shaped product . the naturally degradable green flowerpot in this example is prepared by the following method , comprising : 1 ) crushing plant fiber adhesive agent , and sieving them with a sieve of 60 - 100 mesh to obtain a sieved material and a sieved adhesive agent respectively , 2 ) mixing fully 60 grams of the above sieved material and 40 grams of the above sieved adhesive agent in a mixer to obtain a mixed material , 3 ) adding 1 gram of zinc stearate as lubricant and 5 - 10 grams of water into the above mixed material , and then stirred fully to obtain a molding material , 4 ) putting the above molding material into a mold heated to 130 - 160 ° c . to press it with a pressure of 15 - 30 mpa for 0 . 4 - 1 . 5 minutes , and conducting an exhaustion during pressing for 1 to 3 times to obtain a shaped product , and 5 ) polishing or burnishing the above shaped products when warm to wipe off burr and drilling drainage hole ( s ) at its bottom , in which the adhesive agent in step 2 ) comprises 10 grams of polyvinyl alcohol ( pva ), 10 grams of polycaprolactone ( pcl ), 10 grams of amino - resin , and 10 grams of oxidized starch .
the present invention discloses a naturally degradable green flowerpot and its making process . the green flowerpot includes crushed plant fiber , adhesive agent and lubricant . the adhesive agent comprises oxidized starch and one or more selected from the group consisting of polyvinyl alcohol , polycaprolactone , and amino resin . the making process thereof includes the following steps : crushing plant fiber , mixing , adding lubricant and water , stirring , molding to form , polishing and drilling holes . the green flower pot can naturally degrade , has the advantages of low production cost and is suitable for planting various flowers especially in large mechanized plantation .