metal vacuum bottles often have the inner and outer bottles , 1 and 2 respectively in fig1 made of stainless steel . in this respect , the outer surface 1a of the inner bottle 1 and / or the inner surface 2a of the outer bottle 2 are often nickel - plated and then silver plated either by a typical plating process or a vapor - deposition process in order to form a membrane or film of reflective material 3 for reducing radiation heat loss . as noted above , such bottles are often heated in an evacuated furnace 4 . the furnace is customarily held at a temperature of about 600 ° c . and maintained at a vacuum of about 10 - 4 - 10 - 5 torr . the bottles are thusly heated for one - two hours or so so that the bottle walls are outgased and the evacuation chamber g between the bottle walls is evacuated through a hole 5 that is cut into the bottom of the bottle . the diameter of the opening 5 has been made relatively large -- 20 mm - 30 mm -- to facilitate evacuation of the evacuation chamber g as nearly as possible to the vacuum in the furnace 4 and to shorten the bottle &# 39 ; s required heating time . after a suitable heating and evacuation period a lid 6 is soldered onto the opening 5 in order to maintain the chamber g &# 39 ; s vacuum after the bottle is removed from the evacuated furnace 4 . the soldering step , however , requires temperatures of about 700 ° c .- 800 ° c . ; and , tends to damage the reflective surfaces la and 2a so as to reduce the structure &# 39 ; s ability to limit radiation heat losses . in this respect , the damage is particularily troublesome if silver is used as the reflective surface , because silver is damaged at temperatures only slightly above 600 ° c . that is , silver has relatively poor heat resistance so that its reflectivity deteriorates along with its adhesion onto the stainless steel or nickel substrate . moreover , this problem of silver deterioration is particularly serious because silver has such reflective ability as opposed to other coating materials that it is silver that is commonly used to prevent radiation heat losses . the silver deterioration is particularly troublesome on the inner surface 2a of the outer bottle 2 . accordingly , since this is the largest surface area of the two bottles , soldering temperatures must be strictly controlled when the reflective surfaces 1a and 2a are of silver . additionally , fluxes are not normally used when the soldering occurs in a vacuum . these factors , coupled with the relatively large diameter of the opening 5 , therefore , make the soldering operation quite difficult . consequently , although the abovedescribed method is relatively common ; the productionefficiency is poor ; the soldered joint is not as airtight as desired ; and , the deterioration of the reflective surfaces results in greater - than - desired radiation heat losses . the method illustrated in fig2 is often used to reduce the first method &# 39 ; s soldering prolems . therein , the furnace 7 and the bottle therein are heated to about 600 ° c . a pinch pipe 8 is connected to the outer bottle , however , so that the vacuum chamber g can be evacuated through the pinch tube 8 which extends outside of the furnace 7 . after evacuation the pipe 8 is conventionally pressed or otherwise pinched together as shown . the portion of the pinch pipe 8 that is external of the pinch is then cut off and soldered . this method has the advantage that soldering temperatures of as high as 700 ° c . can be used without too much damage to the silvered or otherwise reflectorized surfaces ; and , flux can be used during the soldering operation . the structure resulting from the method described in connection with fig2 has a natural drawback , however , in that the remaining soldered portion of the pinch pipe 8 must be protected by a cover such as 9 ( fig3 ). this cover not only adds to the cost of the resulting vacuum bottle , but is also bulky in that it adds the voluum 10 which undesirably increases the overall size of the vacuum bottle . in connection with the instant invention a considerable testing program was conducted to determine correlations between the size and number of openings , and the rate at which the vacuum in chamber g was developed during heating in the evacuated furnace 4 . those tests showed that improved - performance vacuum bottles can be obtained without either the large hole 5 or the pinch tube 8 . in this respect , it has been found that the chamber g can be rapidly evacuated even though the outer bottle 2 is pierced as at 11 ( fig4 and 5 ) by only a small hole or holes . in fact , it has been found that holes as small as 0 . 3 mm - 1 . 0 mm in diameter can be used without increasing the time for the chamber g to be evacuated to about the same level of vacuum as is obtained through the methods illustrated in fig1 and 2 . as illustrated in fig4 and 5 , for example , 2 or 3 0 . 3 mm - 1 . 0 mm diameter holes permitted the chamber g to be evacuated to about the level of vacuum in the furnace 4 in the same length of time as the 20 mm - 30 mm diameter opening of fig1 . in one embodiment the outer and inner bottles 1 and 2 were made of 0 . 5 mm thick sus 304 stainless steel . the stainless steel was nickel plated and a layer of silver such as 3 was deposited on the nickel - plated surfaces so that they would be reflectorized . three small openings 11 ( 0 . 3 mm - 0 . 5 mm in diameter ) were pierced in the bottom portion of the outer bottle 2 as shown in fig4 and 5 . the thusly plated bottles 1 and 2 were then assembled as shown and heated in a furnace 4 at a temperature of 580 ° c .- 600 ° c . for 30 - 60 minutes at a vacuum of 10 - 4 - 10 - 5 torr . other examples falling within the above time - temperperature - vacuum limits included as many as 5 0 . 3mm - 0 . 5 mm diameter openings 11 . in each case the heated , evacuated bottles were then moved into an adjoining evacuated apparatus 12 where the small openings 11 in the bottoms of the outer bottles 2 were closed by an electron - beam welder 13 extending into the evacuated apparatus 12 . in this regard , the apparatus 12 and the furnace 4 were separated from each other , but the vacuums in the two were the same . hence , the electron - beam welder 13 could just as easily have been placed in the furnace 4 . the electron - beam welder 13 was of the conventional type employed in precision machinery except that the gun portion included a device for maintaining the vacuum - integrity of the evacuated apparatus 12 where the electron - beam welder 13 extended into the apparatus 12 . the diameter of the inner wall of the the above - described embodiments was 100 mm and the diameter of the outer bottle was 121 mm . inasmuch as the walls were 0 . 5 mm thick , the space between the inner and outer bottles was 10 mm and , the height was such that the capacity of the vacuum bottles was 2 . 2 liters . in &# 34 ; comparison &# 34 ; bottles about to be described , only the outer surface 1a of the inner bottle 1 was nickel and silver plated ; and , 3 0 . 5 mm diameter openings 11 were employed . the vacuum in the furnace 4 was 10 - 5 torr ; and , the vessels were maintained in the heated , evacuated furnace for an hour prior to being moved to the evacuated apparatus 12 which was also maintained at a vacuum of 10 - 5 torr . at that time the vacuums in the chambers g were between 10 - 4 and 5 × 10 - 4 torr . the three small openings 11 were then sealed by electron - beam welder 13 . &# 34 ; standard &# 34 ; bottles manufactured in accordance with the fig1 method had an opening 5 of 20 mm in diameter instead of the small holes 11 . the &# 34 ; standard &# 34 ; structures were evacuated and heated in the same manner as for the comparison embodiments and the lids 6 were then soldered on using silver solder having a melting point of 650 ° c .- 700 ° c . the resulting vacuum in the space g was essentially the same as for the comparison bottles . the insulation qualities of the standard and comparison bottles were then compared by placing 95 ° c . water in each of them for a period of 24 hours . at the end of that time the bottles sealed by the method of the present invention had maintained their contents at between 62 ° c . and 64 ° c . while the standard bottles had only maintained their contents at between 60 ° c . and 61 ° c . in this regard , the small superiority of the method of the invention results from the lack of damage to the silver layer 3 which leads to the reduction in the radiation heat losses obtained by the method of the invention . additionally , the present invention provides a sealing operation that is far more efficient than conventional silver soldering methods . in this regard , the electron - beam welder is about five - to - eight times as efficient as conventional silver soldering methods . moreover , conventional silver soldering techniques sometimes result in such damage that the resulting product must be rejected . accordingly , the method of the invention is additionally desirable for this reason . still further , because of the small size of the holes , the instant invention leaves a smaller area for leaks to occur in the vacuum so that the vacuum lasts longer .
a method of evacuating and sealing the vacuum chamber of a stainless steel vacuum bottle includes the steps of piercing the outer bottle with only very small openings into the vacuum chamber and closing the openings by means of an electron - beam welder after the bottle is heated and the vacuum chamber evacuated .