the method for suturing , repairing and sealing ocular structures according to the present invention involves the use of flaps , as will be described in more detail later on , of biocompatible biological tissue that are applied and welded over a discontinuity or perforation in said ocular structures using a laser - induced welding method . having to operate in a liquid environment , such as the anterior chamber of the eye , the staining solution needed to ensure a selective absorption of the laser radiation cannot be applied topically to the two sides of tissue to be welded . moreover , no liquid must come between the tissues to be welded during the welding process . according to a preferred embodiment of the present invention , the flaps of tissue used for said purpose can be prepared from capsule tissue , particularly flaps of anterior capsule explanted post - mortem from a human donor ( 10 micron thick ) or porcine tissue ( 30 micron thick ). said tissue consists essentially of collagen and elastin , with a limited cellular component , which is usually removed by washing at the time of its explantation . alternatively , other natural biological tissues , such as amniotic membrane , or artificial tissues composed of collagen and / or elastin and suitably structured so as to reproduce the morphology , transparency and mechanical resistance of the above - mentioned natural tissues , may also be used ( see for instance : b . p . chan , “ a photochemical crosslinking technology for tissue engineering — enhancement of the physico - chemical properties of collagen - based scaffolds ”, proceedings of spie volume 5695 , pp . 317 - 327 ( 2005 )). for the sake of simplicity , in the following description reference will only be made to natural flaps of anterior capsule in the shape of a circular disc approximately 2 mm in diameter and a few tens micron thick . the method for preparing the flap is described in detail . when the capsule is explanted from the donor , the flap of anterior capsule is spread on a microscope slide , with the original inner surface uppermost , since this is the one to stain with the chromophore . it is essential to control the flap &# 39 ; s orientation throughout the preparatory stages in order to ensure that the donor flap is repositioned on the recipient capsule so that the curvatures of the two surfaces coincide , since this facilitates a better adhesion . then the chromophore can be applied . the choice of chromophore to use depends strictly on the type of laser that will be used because the absorption band of the chromophore has to include the emission wavelength of the laser to achieve the chromophore - mediated laser welding . in one possible embodiment , the chromophore consists of a sterile water solution of indocyanine green ( indicated below by the abbreviation icg ), a substance widely used in ophthalic surgery , both as a contrast medium and as a photosensitizer , so its toxicological features are well known . from the point of view of its optical properties , icg has strong absorption features at near infrared wavelengths , around 800 nanometers . as known to a person skilled in the art , the shape of the absorption spectrum curve for icg depends on the type of solvent used , the concentration of icg in the solution ( see for instance : m . l . j . landsman , g . kwant , g . a . mook , w . g . zijlstra , “ light - absorbing properties , stability , and spectral stabilization of indocyanine green ”, j . appl . physiol . 40 , pp . 575 - 583 ( 1976 )], and finally on the type of tissue to which the icg binds . to obtain an efficient laser welding of the tissue stained with icg , it is consequently fundamental to identify the optimal concentration of icg in the solution to use beforehand , and subsequently have an apparatus available ( preferably a portable unit suitable for use in the operating room ) to check whether the flap stained with the solution has the right absorption coefficient for the wavelength of the laser generator . in a possible embodiment of the present invention , the staining procedure is as follows : the flap is placed on the glass slide and kept adequately hydrated ; using a calibrated microsyringe a drop of stain solution is applied to the exposed surface , taking care to avoid it spreading beyond the edges and thus staining the underside of the flap in contact with the glass . the drop is left in place for a few minutes ( said time is optimized according to the type of tissue being used , typically 10 minutes for the example described herein ) to allow for the stain to be absorbed by the exposed surface of the tissue . then the flap is abundantly washed with sterile water to remove any residual traces of unabsorbed stain . the result is a flap stained only on the exposed side , which is the side that will be placed in contact with the surface of the recipient capsule when the laser - induced welding is performed . then measurements are taken to characterize the absorption spectrum of the stained flap . a laboratory spectrophotometer can be used to take the preliminary measurements for the preclinical optimization procedure , placing the stained flap in a normal analysis cell . as an example , the continuous line in fig1 shows the typical absorption spectrum for a flap of porcine anterior capsule stained with one drop of a sterile water solution of icg 4 . 4 % left in place for 10 minutes before it was washed and measured with the spectrophotometer . the spectrum clearly shows a wide absorption band between 700 and 800 nanometers , in which there can be comprised the emissions of various types of laser for the welding procedure , such as the aluminium gallium arsenide ( algaas ) diode laser , which has an emission at approximately 800 nanometers , good efficiency characteristics and a more than adequate power rating for the needs of the present invention . in the description that follows , reference is made to this type of laser as the chosen source of radiation . after identifying the icg &# 39 ; s optimal concentration and application times on the flap , the flaps to use in surgical practice in humans can be checked using an instrumentation of the type illustrated in fig2 , which has the advantage of being portable and not contaminating the flaps already sterilized for clinical use . with reference to the figure , the instrument comprises an illuminator 1 , consisting of a tungsten - krypton lamp , for instance , with an optical fiber 2 for illuminating the capsule flap tissue contained in a sterile cell 3 made of transparent plastic material . the light that passes through the tissue is collected by a second optical fiber 4 , connected to a portable spectrometer 5 ( for instance , the illuminator lamp and spectrometer can be the tungsten - krypton sl1 light source and the portable spectrometer mod . epp - 2000 - vis - 100 manufactured by stellar net inc ., usa ). the spectrometer acquires the absorption spectrum of the stained flap , which is then saved on a computer 6 . after testing in this way , the flap can be used immediately for surgery , or it can be preserved , e . g . snap frozen in liquid nitrogen or dehydrated . with reference to fig1 , the dotted line shows the absorption spectrum of a flap of capsule that was dehydrated after staining and then rehydrated seven days later . it is possible to notice that the curve does not differ substantially from that of the fresh tissue , represented by the continuous line . the equipment forming the laser system for welding biological tissues , schematically illustrated in fig3 , comprises a laser 15 with a fiber - optic transmission 14 and an applicator handpiece 7 . in a possible embodiment , said laser may be , as mentioned earlier , an algaas diode laser emitting at 810 nm and a power of 0 . 5 - 10 w , capable of both continuous and pulsing operation , such as the smarty a - 800 laser manufactured by el . en . spa of calenzano ( fi ), italy . said laser beam is transmitted via an optical fiber 14 with a 200 micron core connected to an applicator handpiece , according to the present invention . fig3 also shows a preferred embodiment of the applicator handpiece used to perform the laser welding of the flap in more detail . the handpiece includes a cylindrical grip 7 with the size of a pen , made of plastic or metal , with a spindle 8 at the rear end for locking the jacket of the optical fiber 14 in place , and a needle 9 at the front end , the terminal part of which is bent axially , with the end of the optical fiber extending therefrom . said handpiece , like the optical fiber , is made of sterilizable materials suitable for clinical uses . referring again to fig3 , which shows a possible use of the handpiece forming the object of the present invention to close a capsulorhexis , the needle 9 is of a suitable length ( e . g . 2 - 3 cm ) for inserting in the anterior chamber of the eye , which is delimited between the cornea 10 and the lens 11 , through a corneal or sclero - corneal tunnel , indicated by the numeral 12 , in order to reach the surface of the lens capsule on which the flap of tissue 13 to be welded has been applied . the bent shape of the needle 9 serves the purpose of enabling a moderate pressure to be exerted on the flap to be welded , thus ensuring a good contact between the flap and the surface of the capsule , expelling any fluid of the anterior chamber from the interface . in fact , this is an essential condition for an efficient laser welding between the surfaces of two biological tissues because , at microscopic level , a direct link has to be created between the collagen fibers on the two surfaces being welded together , thanks to the photo - thermal effect induced by the laser radiation . on this aspect , staining only the side of the flap coming into contact with the surface of the recipient capsule serves to ensure that the laser radiation is only absorbed at the interface between said surfaces , so that the welding effect is highly localized and selective , with the advantage of enabling a reduction in the dose of laser radiation needed to complete the weld and thus also minimizing the risk of heat damage to the tissues adjacent to the treated area . the absorption of the chromophore only on the surface interfacing with that of the capsular tissue , as described in the preparation of the materials , and the absence of any gap between the interfaces to be welded , ensured by the fact that the laser radiation is performed with the optical fiber in contact and exerting a moderate pressure that removes any liquid coming between the two surfaces , make it possible to obtain a laser welding of tissues even in a liquid environment such as that of the anterior chamber of the eye . moreover , the end of the optical fiber does not become soiled by said contact because the stained surface is the one on the other side of the flap , facing the surface of the capsule . thanks to said radiation by contact , the welding spot can be perfectly controlled both in terms of shape and size ( the spot welds correspond exactly to the delivery area of the fiber , which is 200 micron in diameter ) and in terms of the laser energy per unit of surface area ( or fluency ) applied to the tissue . in fact , this avoids any variability in the distance of the fiber from the irradiated surface , which affects the fluency because the emission of the fiber is inherently diverging . this makes the application of the laser welding highly reproducible . the method for preparing the flaps and the equipment for the laser - induced welding of said flaps to ocular tissues according to the present invention consequently enables the creation of a valve and the sealing of a capsulorhexis , as needed , for instance , in the surgical procedure based on the phaco - ersatz technique . fig4 , 5 , 6 , 7 and 8 show the principal steps in said procedure , and schematically illustrate the anterior chamber of the eye as seen through the cornea . in particular , fig4 shows the preparation of an access route into the anterior chamber using a method similar to the one adopted in cataract phaco - emulsification surgery , i . e . by means of a sclero - corneal tunnel 16 created surgically with a precalibrated scalpel ( 2 . 75 - 3 . 5 mm wide ); one or two narrower ( 1 mm ) additional service channels , indicated by the numerals 17 and 18 in fig4 , are usually also created to facilitate intraocular maneuvers . the next step , as illustrated in fig5 , is the capsulorhexis approximately 1 mm in diameter on the anterior capsule . said rhexis is used to aspirate the contents of the lens , e . g . using a phaco - emulsifier as illustrated in fig6 , then the capsule can be refilled with hyaluronic acid , injected through the capsulorhexis . the tissue flap prepared as explained earlier is then inserted through the sclero - corneal tunnel 16 and positioned on the anterior capsule , as schematically shown in fig7 , with the aid of microtweezers , so as to cover the rhexis entirely . great care is taken during this step to ensure that the stained side faces the surface of the capsule . as shown in fig8 , the flap is welded around the circumference of the rhexis using the applicator handpiece and the radiation technique previously described , according to the present invention . in the example in fig8 , the welding is completed by means of adjacent spot welds . instead of completing the weld around the full circumference of the flap , one quadrant of the flap is initially left free . the partially welded flap thus serves as a valve through which the capsule can subsequently be filled with a biocompatible polymer , as shown in fig9 . finally , the valve is closed using the method already illustrated in fig8 , completing the welding around the full circumference so as to seal in the contents . where necessary , the polymer used to fill the capsule can be submitted to irradiation from the outside to induce its polymerization without any need to remove the capsule at the end of said operation . it should be noted that the welding can only be done efficiently for certain laser emission parameters , which depend on the type of tissue being irradiated and the concentration of stain . referring to the preferred embodiment described herein , as a non - limiting example , a pulsing radiation method can be used for the laser - induced welding of capsule tissue , instead of the continuous irradiation more frequently used for other types of tissue . said pulsing mode is particularly suitable for the contact - type welding procedure forming the object of the present invention and has the advantage of reducing the interaction time with the ocular structures , which are particularly vulnerable , thereby limiting the propagation of heat to the adjacent tissues and the related risk of heat damage . typical parameters for use with this irradiation method are , for instance : a pulse duration between 50 and 150 ms , with a single - pulse energy coming between 20 and 100 millijoules . finally , it should be noted that the method according to the present invention can also be advantageously applied to fix corneal or intraocular prostheses , e . g . contact lenses , iol , and so on , as well as to contain retinal detachments or seal retinal perforations . variations and modifications of the present invention may be appreciated based on a review of the description . any such changes and additions are intended to be within the spirit and scope of the present invention , as defined by in the following claims .
a method of suturing the lens capsule of the eye in the event of accidental rupture thereof or to create a valve and / or to close a capsulorhexis by laser - induced welding onto the capsule &# 39 ; s surface of a flap of biocompatible biological tissue prepared so as to be optically absorbent at the wavelength of the laser being used for welding . the method is suitable for use in so - called phaco - ersatz or “ lens refilling ” ophthalmologic surgery . welding is desirably performed using laser devices that comprise a laser generator and a fiberoptic system for conveying the laser beam , complete with an applicator handpiece suitable for use in welding the flaps onto the lens capsule in a liquid environment . the handpiece is shaped so as to exert moderate pressure on the tissues to be welded with the free end of the optic fiber .