a hermetic sachet of low density polyethylene , of 40 μm in thickness and of 50 cm 2 surface area , containing 0 . 5 g of cuprous oxide , were introduced into a 60 ml bottle . 30 ml of an aqueous thioglycolic acid solution at a concentration of 184 g / l ( 2m ) are next introduced . the bottle is closed ; after closing it contains 30 ml of air . an identical bottle , but not containing a deodorizing sachet , is simultaneously prepared . the two bottles are stored at ordinary temperature and the h 2 s content in these two bottles is evaluated by &# 34 ; head space &# 34 ; gas phase chromatography by measuring , during the storage , the height of the corresponding peak , the value of the height of the peak being arbitrary . the results obtained are given in the appended fig1 . in this figure , the storage time in days is placed on the abscissa and the height of the peak corresponding to h 2 s obtained by &# 34 ; head space &# 34 ; gas phase chromatography is placed on the ordinate . the curve ( 1 ) corresponds to the control bottle not containing a deodorizing sachet and the curve ( 2 ) to the bottle containing a deodorizing assembly according to the invention . it is observed that there is practically no h 2 s contained in the bottle containing the sachet ; the deodorization is very efficient . a deodorizing assembly consisting of a hermetically sealed , low density polyethylene sachet having a thickness of 300 μm and a surface area of 40 cm 2 and containing 200 mg of finely divided cuprous oxide is placed in a bottle of 33 ml capacity . 25 ml of thioglycolic acid in aqueous solution at a concentration of 92 g / l ( 1m ) is next introduced . the initial content of h 2 s and of methanethiol is measured by &# 34 ; head space &# 34 ; gas phase chromatography . the air is flushed from the bottle using a stream of nitrogen and the bottle is closed hermetically and stored at ambient temperature . at the end of 18 hours , the content of h 2 s and of methanethiol is measured by &# 34 ; head space &# 34 ; gas phase chromatography . the h 2 s content is equal to 6 . 5 % of the initial value and the presence of methanethiol can no longer be detected . at the end of 48 hours , the ph of the solution is adjusted to a value of 9 using monoethanolamine : it then becomes possible to detect by nose the faintly ammoniacal odor of the base , which is not masked by any malodorous compound . a bottle with a capacity of 60 ml is used . a deodorizing assembly consisting of a sachet of a butadiene - styrene copolymer , marketed under the trade name &# 34 ; styrolux kr 2688 &# 34 ; 0 by the company &# 34 ; basf &# 34 ;, of 40 μm in thickness and of 50 cm 2 surface area containing 500 mg of cuprous oxide at a concentration of 97 % by weight is introduced into this bottle . 40 ml of an aqueous solution of thioglycolic acid at a concentration of 184 g / l ( equivalent to 2m ) is next introduced . the bottle is then sealed : it contains 20 ml of air . the h 2 s content was measured by &# 34 ; head space &# 34 ; gas phase chromatography at the start , at the end of two days and at the end of 16 days . it was observed that , at the end of two days , the h 2 s concentration is only 19 . 7 % of the starting concentration and that , after 16 days , it is only 0 . 6 % of the starting concentration . it is thus observed that , despite the presence of air in the bottle , which promotes the formation of hydrogen sulphide , the h 2 s content has been brought to a very low value . a deodorizing assembly consisting of a sachet made of a butadiene - styrene copolymer , marketed under the trade name &# 34 ; styrolux kr 2688 &# 34 ; by the company &# 34 ; basf &# 34 ;, of 40 μm in thickness and of 50 cm 2 surface area was introduced into a bottle of 60 ml capacity . the sachet contains 2 . 0 g of active charcoal marketed under the trade name &# 34 ; acticarbone acf3 &# 34 ; by the company &# 34 ; ceca &# 34 ;. 30 ml of an aqueous solution of thioglycolic acid at a concentration of 184 g / l ( 2m ) is next introduced into the bottle . the bottle is sealed . it then contains 30 ml of air . an identical bottle , but not containing a deodorizing sachet , was simultaneously prepared . the two bottles were stored at ambient temperature . the hydrogen sulphide content was measured by &# 34 ; head space &# 34 ; gas phase chromatography . it was observed that , at the end of 3 days , the h 2 s content in the bottle containing the deodorizing sachet is 4 . 5 % of that in the bottle not containing a deodorizing sachet ; after storage for 10 days , this content is only 2 % and after 20 days , it is only 0 . 1 %. a hermetically sealed sachet made of a butadiene - styrene copolymer marketed by the company &# 34 ; basf &# 34 ; under the trade name &# 34 ; styrolux kr 2688 &# 34 ;, of 40 μm in thickness and of 50 cm 2 surface area , containing 1 . 5 g of a mixture of active charcoal , charcoal and cuprous oxide at a concentration of 97 % by weight , the ( active charcoal - charcoal / cuprous oxide ) ratio by weight being 2 / 1 , was introduced into a 60 ml bottle . 30 ml of a thioglycolic acid solution at a concentration of 184 g / l ( 2m ) is next added . the bottle is sealed ; it contains 30 ml of air . as in the above example , an identical bottle , but not containing a deodorizing sachet , is simultaneously prepared . the two bottles are kept at ambient temperature . the h 2 s content in each of the two bottles was measured by &# 34 ; head space &# 34 ; gas phase chromatography . it was observed that , at the end of 3 days , the h 2 s content in the bottle containing the deodorizing sachet is 7 % of that in the unit not containing a deodorizing sachet , that it is only 2 % at the end of 10 days and 0 . 15 % at the end of 20 days . a sachet made of low density polyethylene of 20 μm in thickness and of 50 cm 2 surface area containing 1 . 8 g of activated alumina marketed by the company &# 34 ; procatalyse &# 34 ; is introduced into a bottle of 60 ml capacity . 30 ml of a thioglycolic acid solution at a concentration of 184 g / l ( 2m ) is next introduced . the bottle is sealed ; it contains approximately 30 ml of air . as in examples 4 and 5 , a control bottle is prepared and the h 2 s content in the two bottles is measured after storage at ambient temperature . it is observed that , at the end of 3 days , the h 2 s content in the bottle containing the deodorizing sachet is only 22 % of that in the control bottle , that after 10 days , it is only 2 % and after 20 days it is still 2 %. a packaging as represented in fig4 is used . the lower bottle 10 contains : ______________________________________thioglycolic acid 9 . 1 gwater qs 50 ga deodorizing sachet identical to that describedin example 1 is introduced into the bottle 10 . the upperbottle 20 contains : 20 % aqueous ammonia ( by weight ) 10 . 4 gammonium hydrogen carbonate 6 . 35 gmixture of cocoamidopropyl betaine and of 0 . 4 g ( am ) glyceryl laurate sold under the trade name &# 34 ; tegobetaine hs &# 34 ; by the company &# 34 ; goldschmidt &# 34 ; in solution at anactive material ( am ) concentration of 30 % oxyethylenated oleyl alcohol 0 . 8 gcontaining 20 moles of ethylene oxidewater qs 50 g______________________________________ the thioglycolic acid solution is mixed just at the time of use . the user of this permanent - wave composition does not detect any unpleasant odor during its use on a head of hair . a permanent reshaping reducing composition for hair is prepared by mixing the following ingredients : ______________________________________thioglycolic acid 9 . 1 gmixture of cocoamidopropyl betaine and of 0 . 4 g ( am ) glyceryl laurate sold under the trade name &# 34 ; tegobetaine hs &# 34 ; by the company &# 34 ; goldschmidt &# 34 ; in solution at anactive material ( am ) concentration of 30 % oxyethylenated oleyl alcohol 0 . 8 gcontaining 20 moles of ethylene oxidewater qs 100 g______________________________________ approximately 75 ml of this solution is applied to wet hair which has been rolled onto curlers beforehand . a cap consisting of a thin double wall made of low density polyethylene , each wall having a thickness of 20 μm and a surface area of 1300 cm 2 is placed on the head of hair . 2 g of a mixture consisting of 1 . 4 g of active charcoal sold under the trade name &# 34 ; as 1544 &# 34 ; by the company &# 34 ; ceca &# 34 ; and 0 . 6 g of cuprous oxide are distributed uniformly between the two walls . the cap is fitted with a securing means . the composition is left to act for 15 minutes , after having covered the head of hair with the cap . it is observed that the cap allows unpleasant odors to be avoided during the permanent - wave reduction phase . after rinsing copiously with water the following oxidizing composition is then applied : ______________________________________hydrogen peroxide 1 . 5 goxyethylenated sodium lauryl ether sulphate 3 . 75 gcontaining 2 moles of ethylene oxidecitric acid 0 . 5 gsodium hydrogen phosphate 0 . 5 gperfume 0 . 3 gdeionized water qs 100 g______________________________________ the oxidizing composition is left to act for approximately 5 minutes and the curlers are then removed and the hair is rinsed copiously with water . after drying under a hair dryer , the hair has beautiful curls .
method of deodorizing in order to remove malodorous compounds which are present in or formed from a liquid formulation containing at least one compound bearing a thiol functional group , of formula : hs -- a -- y -- b in which : 1 ) the liquid formulation is placed in contact with an inert membrane which is permeable to the malodorous compounds and impermeable to the compound of formula ; and 2 ) the malodorous compounds which have passed through the membrane are placed in contact with at least one chemical substance reacting with the said malodorous compounds and / or with at least one physical adsorption substance having a large specific surface area which binds the said malodorous compounds .