in accordance with the present invention , a wax is provided which is in a fine powdered state having an average particle size of less than about 100 microns and preferably less than about 90 microns . the powdered wax of the invention is preferably comprised of beeswax ( also referred to as white wax ), or mixtures of beeswax and carnauba wax , although one or more other waxes may be employed in combination with the beeswax and / or carnauba wax or by themselves . examples of such other waxes suitable for use herein include , but are not limited to , paraffin wax , polyethylene glycol waxes , other hard waxes such as candelilla wax , ozokerite , oricury , microcrystalline wax and the like . the powdered wax of the invention may be applied as a polish to tablets to produce a durable shiny protective coating . furthermore , the wax coating may be printed over with the print being retained for extended periods of time . in fact , the overall appearance and durability of both the print and shine is superior to that of conventionally wax - coated and printed tablets . in addition , in accordance with the present invention , a method is provided for preparing the powdered wax described above , which method includes the steps of providing a desired wax formulation , melting the wax formulation to form a homogeneous mass , allowing the wax formulation to harden , breaking the hardened wax formulation into small pieces , milling the small pieces of wax with dry ice employing a weight ratio of wax to dry ice of within the range of from about 0 . 5 : 1 to about 5 : 1 , preferably from about 0 . 5 : 1 to about 2 : 1 , and then allowing the dry ice to evaporate from the milled wax formulation while maintaining the wax at a temperature of below about 5 ° c ., thereby leaving the wax in a fine powdered state free of clumps . in carrying out the above method , the homogeneous melted wax formulation is preferably frozen before it is broken up into small chunks prior to milling . the size of the small chunks of wax to be milled is not critical . however , for convenience , it is preferred that the wax be broken up into pieces of from about 1 to 5 microns up to about 1 to 10 centimeters in size to facilitate milling . the milling of the frozen pieces of wax with dry ice is carried out employing conventional high speed milling apparatus such as a fitzpatrick mill employing hammers forward through a small herring bone screen . however , other conventional milling equipment may be employed as will be apparent to those skilled in the art . the milling procedure may be carried out as a one step procedure . however , it is preferred that the milling step be carried out stepwise so that a first portion of the dry ice will first be milled , thereafter a second larger portion of dry ice together with milled dry ice will be mixed with the wax chunks and the mix milled , and finally the remainder of the dry ice will be milled with the wax - dry ice mixture . after the wax is milled with dry ice , a snow of dry ice and wax is formed which is kept in a cooled state as the dry ice is allowed to evaporate . the snow may be placed in conventional refrigeration apparatus to maintain the snow at a temperature of within the range of from about - 5 ° to about 5 ° c . if during the dry ice evaporation period , the wax is allowed to reach temperatures of greater than about 10 ° c ., the wax will form clumps as opposed to the desired fine powder . the powdered wax produced by the method of the present invention is particularly suited as a polishing agent and print substrate for tablets . in fact , heretofore , where it has been attempted to powder wax , the result has been melted globs or a semi - powder - like wax product replete with clumps and therefore unsatisfactory as a polishing agent for tablets . the following examples represent preferred embodiments of the present invention . all temperatures are expressed in ° c . a fine powdered wax containing equal parts of carnauba wax and white wax particularly suitable for use as a polishing agent for sugar - coated tablets was prepared as described below . carnauba wax ( 10 kg ) and white wax ( 10 kg ) were placed in a suitably sized container and melted at 100 °. the melted homogeneous wax mix was then placed in a freezer maintained at - 10 ° c . for four hours . the resulting frozen block of wax was removed from the freezer , placed in a cloth and then broken into small chunks of average size of less than 2 inches . the wax chunks were immediately milled with dry ice in a fitzpatrick impact mill with hammers forward high speed through a 0 . 15 &# 34 ; by 17 / 32 &# 34 ; long herring - bone or finer herring - bone screen , as follows . 1 kg of milled dry ice was milled with 13 kg of dry ice chunks together with all 20 kg of the wax mix . thereafter , the milled dry ice - wax mix was milled with another 1 kg portion of dry ice . a dry ice / wax snow was thereby formed which was spread on a tray . the tray was placed in a refrigerator maintained at about 4 ° c ., for 12 hours , thereby allowing the dry ice to evaporate and leaving fluffy powdered wax having a fineness of 100 % through # 60 mesh screen and over 25 % through # 400 mesh screen on an alpine sieve . the so - formed powdered wax was placed in an air - tight container and refrigerated until used . the 50 -- 50 carnauba wax - white wax powder was applied as a polishing agent for sugar coated tablets to produce a durable quality shiny coating without the need for use of chlorinated hydrocarbon solvents or flammable hydrocarbon solvents . the so - polished tablets were printed over to form a durable print which was not easily rubbed off . a fine powdered pure white ( beeswax ) wax was formed employing the procedure as described in example 1 except that all carnauba wax was replaced with white wax . the resulting powdered white wax was found to be of the same fineness as the example 1 wax .
a novel powdered wax is provided which is especially adapted for use as a polishing agent for tablets and as a substrate for print carried by such tablets . a method for forming such powdered wax is also provided which includes the steps of milling pieces of wax with dry ice and then allowing the dry ice to evaporate while maintaining the milled wax at cool temperatures to prevent clumping .