the invention relates to an amorphous solidifying precious metal alloy containing platinum and / or palladium , a method for its production as well as an article made on the basis of said precious metal alloy , in particular ornamental articles like a piece of jewelry , a watch , a watch case or a writing instrument . amorphous solidifying precious metal alloys based on precious metals are increasingly used , in particular in the jewelry or watch making industry , since they have an unusual combination of mechanical properties , in particular in respect to their hardness and elasticity , which is not achieved by any other material known up to now . often amorphous solidifying precious metal alloys are characterized in comparison to conventional crystalline precious metal alloys of a comparable composition , by a significantly higher hardness . a further advantage of amorphous solidifying metals is a combination of the mechanical properties with the possibility of a near net shape processing by casting or thermoplastic forming : the processing of such amorphous solidifying metals is performed without solidification shrinkage and leads to mechanically high loadable work - pieces . when casting such amorphous solidifying metals , the maximum achievable thickness of completely amorphous solidified workpieces is limited by the critical cooling rate of the respective precious metal alloy . by means of thermoplastic forming amorphous workpieces can be deformed or joined above the glass transition temperature t g , so that in this way thin - walled , hollow , large - area and / or surface structured workpieces having dimensions beyond the critical thickness can be made . the first amorphous precious metal alloy based on precious metals was a binary precious metal alloy in au - si - system . starting from this system , the up to now most well - known amorphous precious metal alloy having the composition au 49 ag 5 , 5 pd 2 , 3 cu 26 , 9 si 16 , 3 was developed by liquidmetal technologies inc ., where the above - mentioned amounts are expressed in atomic percent . in terms of mass percent , this corresponds to au 76 , 3 ag 4 , 7 pd 1 , 9 cu 13 , 5 si 3 , 6 . this precious metal alloy having an amount of gold of 18 carat exhibits a hardness of 360 hv and exceeds the hardness value of a comparable crystalline precious metal alloy by more than 50 %. a disadvantage of said precious metal alloy was an insufficient corrosion behavior , which is why this precious metal alloy was not widely used . furthermore , precious metal alloys on a platinum basis are known , e g . pt 42 , 5 cu 27 ni 9 , 5 p 21 as well as pt 60 cu 16 co 2 p 22 , whereby the afore - mentioned amounts are once more expressed in atomic percent . in terms of mass percent , this corresponds to pt 73 , 9 cu 15 , 3 ni 5 p 5 , 8 and pt 86 , 6 cu 4 , 5 co 0 , 9 p 5 respectively . this exclusively top - class precious metal alloys exhibit unusual high hardnesses of above 400 hv too . they are more corrosion resistant , when compared to the afore - mentioned amorphous solidifying gold alloys , due to a generally slower kinetics . the main disadvantage of said known amorphous precious metal alloys on a platinum basis is their large admixture with nickel - phosphor or phosphor respectively , which is disadvantageous to processing and recycling . in the afore - mentioned platinum alloys e . g . nickel - phosphor amounts and phosphor amounts of 21 and 22 atomic percent respectively are required in order to achieve a sufficient glass forming ability and lowest liquidus temperatures respectively in the system pt — p . furthermore amorphous solidifying precious metal alloys on a palladium basis are known , e . g . pd 40 co 30 ni 10 p 20 , wherein the amounts of the afore - mentioned alloy components are expressed in atomic percent once more . expressed in mass percent , the afore - mentioned precious metal alloy has got the following composition : pd 58 co 26 ni 8 p 8 . in this case once more the high amount of nickel - phosphor of together approximately 16 mass percent is disadvantageous . u . s . pat . no . 4 , 746 , 584 a1 describes metal electrodes , which are made of an amorphous metal according to the formula pt p a a d d , wherein a stands for iridium , palladium , rhodium , ruthenium or a mixture thereof and d stands for boron , aluminum , arsenic , phosphor , antimony , germanium , silicon or a mixture thereof . the mass amount p is between 40 - 82 %, the mass amount a between 1 - 40 % and the one of d between 8 - 40 %, whereby the amounts of p , a and d supplement to 100 wt .-%. this amorphous precious metal alloy is characterized in that it always contains two elements of the platinum group , namely always platinum and a further element of the platinum group . from ep 0 267 318 a2 a crystalline precious metal alloy for jewelry purposes is known , which consists of 75 wt .-% to 99 , 5 wt .-% palladium as a basic metal and additives of metals of the 3 . to 6 . period of the periodic system of the elements . de 20 2009 013 202 u1 describes a crystalline platinum jewelry alloy , which comprises 50 wt .-% to 70 wt .-% platinum , 2 wt .-% to 15 wt .-% of at least one metal , chosen from the group indium , gallium , germanium , tin and zinc , and 0 , 5 wt .-% to 40 wt .-% silver or copper . de 10 2007 006 623 a1 describes a crystalline platinum alloy for the manufacturing of jewelry items , having the following composition , whereby the amounts given are in terms of weight - percent : 39 - 66 % platinum , 5 - 30 % palladium and 10 - 32 % copper . preferred embodiments of such alloys provide a composition of 44 - 46 % platinum , 9 - 30 % palladium and 24 - 27 % copper and 39 - 41 % platinum , 9 - 30 % palladium and 29 - 52 copper respectively . it is the object of the present invention to create an amorphous solidifying precious metal alloy , which — apart from unavoidable mixtures and impurities — is free of nickel and / or phosphor . furthermore , a method for the production of a semi - finished product made of the inventive precious metal alloy is to be provided . further objects of the invention are to provide a semi - finished product , in particular for the production of jewelry , as well as the use of the inventive precious metal alloy for the manufacturing of an ornamental article as well as to provide an ornamental article . the precious metal alloy according to the invention is characterized by a composition according to a a b b c c , whereby a is at least one element of a group consisting of pt and pd , b is at least one element of a group , which consists of al , au , ag , cu , and c is at least one element of a group , which consists of ga and ge , whereby the mass amount a is between 45 - 60 mass percent , preferably between 45 - 59 mass percent , further preferably between 48 and 54 mass percent , the mass amount b is between 39 - 55 mass percent , preferably between 39 - 49 mass percent , further preferably between 40 to 47 mass percent , and the mass amount c is between 0 - 13 mass percent , preferably between 1 - 13 mass percent , further preferably between 2 to 10 mass percent and in particular preferably between 2 to 5 mass percent , whereby preferably , when platinum and palladium are simultaneously present , the precious metal alloy does not comprise aluminum as the sole alloy component of the group b , and whereby the afore - said amounts a , b and c , apart from usual admixtures and impurities , supplement to 100 mass percent . by the inventive measures a platinum alloy is provided , which is free of nickel and / or phosphor , but still has a good glass forming ability . the inventive precious metal alloy is characterized by a high corrosion and tarnish resistance and is therefore , in particular , suited for the manufacturing of high quality workpieces such as e . g . jewelry articles . surprisingly , it has been found that these advantageous properties not only appear when platinum is used as a basis material , but also with palladium or a mixture of platinum and palladium , wherein the amount of palladium and platinum and palladium respectively is between 45 to 60 mass percent . the precious metal alloys according to the invention have got the advantage that they do not contain nickel and / or phosphor . this simplifies their manufacturing and a metal recycling considerably . the precious metal alloys furthermore are unproblematic in respect to allergies , which is in particular of advantage in their application in the jewelry and watch making industry , where the respective ornamental pieces are often imminent and for a long period of time in direct contact with the skin . the method for producing a semi - finished product from an amorphous solidifying precious metal alloy according to the invention provides that a mass amounts of at least one element of said group a , b mass amounts of at least one element of the aforesaid group b and c mass amounts of at least one element of afore - mentioned group c are alloyed and cast to the semi - finished product . the semi - finished product according to the invention provides that it is made of the aforedescribed precious metal alloy according to the invention . according to the invention , for manufacturing an ornamental article , in particular a piece of jewelry , a watch , a watch case , a watch band , a writing instrument or a part of such an item , an amorphous solidifying precious metal alloy is used , which is characterized by the composition aa bb cc , whereby a designates at least one precious metal of a group consisting of platinum and palladium , b designates at least one element of a group consisting of al , au , ag and cu , c designates at least one element of a group consisting of ga and ge , whereby the mass amount a is in the range of 45 - 60 mass percent , preferably in the range of 45 - 59 mass percent , further preferably in the range of 48 to 54 mass percent , the mass amount b is in the range between 39 - 55 mass percent , preferably in the range of 39 - 49 mass percent , further preferably in the range of 40 to 47 mass percent , and the mass amount c is in the range of 0 - 13 mass percent , preferably in the range of 1 - 13 mass percent , further preferably in the range of 2 to 10 mass percent , and in particular preferably in the range of 2 to 5 mass percent , whereby preferably , when platinum and palladium are simultaneously present , the amorphous precious metal alloy does not contain aluminum as a single alloy component of the group b , and wherein the afore - mentioned mass amounts a , b and c , apart from usual admixtures , impurities and alloy tolerances , supplement to 100 mass percent . the ornamental article according to the invention , in particular jewelry like a jewelry item , a watch , a watch case , a watch band , a writing instrument or a part of said articles provides that this article is entirely or partially made of an amorphous precious metal alloy according to the invention . further advantageous developments of the invention are the subject matter of the dependent claims . further details and advantages of the invention are disclosed in the exemplary embodiments , which are described below ; the following values of amounts are mass percentages . the first three exemplary embodiments of a precious metal alloy based on platinum belong to the system pt — a — cu . a first exemplary embodiment of a precious metal alloy based on platinum is given by pt 53 , 2 ag 31 , 4 cu 12 , 2 ga 3 , 2 . this precious metal alloy is characterized by a favorable glass forming ability . a second exemplary embodiment provides that the precious metal alloy is given by pt 50 ag 33 , 8 cu 13 , 2 ga 3 . a third exemplary embodiment of a precious metal alloy is given by pt 50 ag 30 , 6 cu 11 , 9 ge 7 , 5 . the next three exemplary embodiments relate to an amorphous solidifying precious metal alloy , whose main components are pt — al — cu . the fourth exemplary embodiment is a precious metal alloy pt 53 , 1 al 35 , 8 cu 7 , 9 ga 3 , 2 . the fifth exemplary embodiment is the precious metal alloy pt 50 al 38 , 5 cu 8 , 5 ga 3 . the sixth exemplary embodiment provides a precious metal alloy pt 50 al 34 , 9 cu 7 , 7 ge 7 , 4 . the seventh and eighth exemplary embodiment each describe a precious metal alloy of the system pt — au — ag — cu . the corresponding precious metal alloy are exemplarily given by pt 50 au 23 , 5 ag 17 cu 6 , 5 ga 3 and pt 50 au 21 , 2 ag 15 , 3 cu 6 ge 7 , 5 . the afore - mentioned eight exemplary embodiments therefore describe amorphous solidifying precious metal alloys based on platinum , which are characterized by the following composition : pt a b b c c , whereby pt stands for platinum , b characterizes at least one element of a group consisting of al , au , ag , and cu , and c defines at least one element of a group consisting of ga and ge . the parameter a stands for the platinum amount of the described precious metal alloy with 45 - 60 mass percent , the parameter b for 39 to 55 mass percent , preferably 39 - 49 mass percent , and the parameter c for 0 - 13 mass percent . it is preferred that platinum is present in an amount of 45 - 60 mass percent , preferably between 45 and 59 mass percent , further preferably between 48 - 54 mass percent , in particular in an amount of 49 to 51 mass percent or 50 - 54 mass percent and for the last range in particular in an amount of 50 - 52 mass percent in the described precious metal alloy . the last mentioned ranges are characterized by a particularly favorable glass forming ability . the amount b of the one or of several metals of the group b is between 39 to 55 mass percent , preferably 39 - 49 mass percent , preferably 40 - 47 mass percent and in particular 42 - 47 mass percent . it is preferred that at least one of gallium and / or germanium is present in an amount c between 0 - 13 mass percent , preferably in an amount of 1 - 13 mass percent , preferably in an amount of 1 - 12 mass percent and here in particular between 2 - 10 mass percent and further in particular 2 to 5 mass percent in the described precious metal alloy . it is possible , but not preferred , that at least one of gallium and / or germanium is present in an amount c of 0 - 1 mass percent , so that in an extreme case ( c = 0 ) gallium and / or germanium is not contained in the afore described precious metal alloy . as mentioned at the beginning , it has surprisingly been shown that not only amorphous solidifying precious metal alloys based on platinum with the afore described composition exhibit the advantageous properties , but that platinum can be completely or partially substituted by palladium . the ninth exemplary embodiment is a precious metal alloy associated to the system pd — ag — cu and consists of pd 50 ag 34 cu 13 ga 3 . in this case too , a favorable glass forming ability is given . an exemplary embodiment of a precious metal alloy associated to this system is pd 50 au 20 , 2 ag 14 , 6 cu 5 , 7 ge 9 , 5 . the afore described precious metal alloy can be characterized by pd a b b c c , whereby pd stands for palladium and b and c once more for at least one element of the afore - mentioned groups al , au , ag , cu and ga , ge respectively . the amount a of palladium is once more between 45 - 60 mass percent , preferably 45 - 59 mass percent , further preferably 48 - 54 mass percent , further preferably 49 - 51 mass percent or 50 - 54 mass percent and hereby preferably 50 - 52 mass percent , whereby in particular in the last mentioned concentration ranges a particularly favorable glass forming ability is given . the amount b of the one or the elements of the group b is between 39 to 55 mass percent , preferably 39 - 49 mass percent , further preferably 40 - 47 mass percent and hereby further preferably 42 - 47 mass percent . the amount of gallium and / or germanium once more is between 0 - 13 mass percent , whereby the preferred ranges , which are specified above under no . 1 for the amorphous precious metal alloys based on platinum apply for palladium correspondingly . it is preferred that the ratio of the atomic proportions of palladium and aluminum is equal or greater 4 . this atomic ratio of palladium to aluminum corresponds to a mass ratio of palladium to aluminum of equal or greater 94 / 6 ; therefore it is preferred that the ratio of the amounts of palladium and aluminum is — expressed in mass ratios — equal or greater 15 , 67 . an example for such an alloy is given by an alloy , which contains 45 to 60 mass percent palladium , 39 to 55 mass percent of at least two elements of the group b and at least one of gallium and / or germanium in an amount of 0 to 13 mass percent , but with the following condition : the first of the at least two metals of the group b is aluminum , whereby aluminum — corresponding to the amount of palladium in the range between 45 to 60 mass percent and the afore - mentioned ratio between palladium and aluminum — is present in an amount of at maximum 45 / 15 , 67 to 60 / 15 , 67 , i . e . in an amount of 2 , 87 to 3 , 83 mass percent ; the rest of the amount b of the at least two elements of the group b is then provided by a further element of the afore - mentioned group b . as in the cases described above , the preferred ranges for the amounts a , b and c apply here correspondingly . a precious metal alloy , which does not only contain platinum or palladium alone , but a combination of platinum and palladium —( pt a1 pd a2 ) a in an amount a = a 1 + a 2 of 45 - 60 mass percent and in addition the afore - mentioned components , in which platinum is substituted by palladium up to 100 wt .-%, exhibits the afore - mentioned advantageous properties too , in particular in respect to the glass forming ability . as an example for such a precious metal alloy pd 50 pd 3 , 2 ag 31 , 4 cu 12 , 2 ga 3 , 2 is to be mentioned . the platinum - palladium - alloys are characterized by ( pt a1 pd a2 ) a b b c c , whereby for the mass amounts a , b and c once more the values disclosed in sections 1 . 3 and 2 . 3 apply . it is once more preferred that the ratio of the atomic amounts of palladium and aluminum is equal or greater than 4 . the explanations at the end of section 2 . 3 also apply for a combination of platinum and palladium correspondingly . as exemplary embodiment the following alloy is to be stated : such alloy contains platinum and palladium in a total amount of 55 mass percent , whereby it is assumed that 50 weight percent platinum and 5 weight percent palladium are present . the amount of elements of the group b , here exemplarily aluminum and copper , is between 40 and 45 mass percent , whereby , if appropriate , a corresponding amount c of elements of the group c is contained . the amount of aluminum then is less than 0 , 32 mass percent and the amount of copper is in the range between 39 , 7 to 24 , 7 mass percent . it is preferred that in the case when platinum and palladium are simultaneously present , one of these two elements , i . e . platinum or palladium , is present in an amount of more than 50 mass percent , in order to maintain the hallmarking capability of such a precious metal alloy with at least 50 mass percent of platinum or palladium , or in an amount of slightly less than 50 mass percent . as an example , the amount of platinum , assuming that the total amount of platinum and palladium is of 51 - 60 mass percent together , can be 50 - 59 mass percent , this means that palladium then is present in an amount of 1 mass percent only . the same applies vice versa , namely , that — once more as an example — palladium is present in an amount of 50 - 59 mass percent and hence the amount of platinum is only 1 mass percent . of course any combinations are possible , e . g . that the amount of platinum and palladium respectively is 50 - 54 mass percent , preferably 50 - 52 mass percent , at a total amount of platinum and palladium of e . g . 59 mass percent , and the rest of the each other metal is then the amount lacking to 59 mass percent . in the foregoing description of the exemplary embodiments of the amorphous platinum - palladium alloys it was assumed that several elements of the group b , i . e . of the group consisting of al , au , ag , cu , is present . but it is possible too that only one of these elements , as a single alloy element , of the group b is present in the described precious metal alloys . but it is preferred that aluminum is not present as the only element of group b . a combination of elements of the group b , which contains al , is possible in said amorphous platinum - palladium alloys , as well as in the afore described amorphous platinum alloys and the amorphous palladium alloys . this is especially true when the amount a of platinum and palladium is between 45 and 59 mass percent , and is in the afore described sub ranges of the amount a . the manufacturing of the afore - mentioned precious metal alloys is , as an example , illustrated with reference to the first embodiment . manufacturing of the further precious metal alloys having the composition a a b b c c is done correspondingly : for the manufacturing of the precious metal alloy of the first exemplary embodiment 53 , 2 mass percent platinum , 31 , 4 mass percent silver , 12 , 2 mass percent copper and 3 , 2 mass percent gallium are alloyed and casted to form a massive semi - finished product . the semi - finished product is then melted in the next step and processed by a rapid solidification process . preferred is an atomization of the melted mass in a flow of inert gas by means of a method and a device , which is e . g . described in the german patent de 103 40 606 b4 . in an atomization of the melted mass with a starting temperature of 1250 ° c . in a nitrogen stream with a discharge pressure of 10 bar the material solidifies in splits of a second in the form of amorphous powders , which typically have an average particle diameter of 25 μm . the amorphous powder has got a glass transition temperature t g of approximately 290 ° c . and a crystallization temperature t x of approximately 450 ° c . further rapid solidification processes are a die - casting as well as a surface coating process such as thermal spraying or cold gas spraying . the further processing of the plastified amorphous semi - finished product masses at temperatures above the glass transition temperature by means of the so called thermoplastic forming under pressure ( tpf - method ), as e . g . the die - casting of plastified amorphous semi - finished product masses by temperatures above the glass transition temperature is possible . it is evident for the person skilled in the art from the above description that the ranges specified in each case apply in the context of conventional alloy tolerances . in addition , it is evident for him that by specifying the range limits all mass portions falling in the respective range are encompassed too . in conclusion , it is to be stated that the described precious metal alloy is in particular suited for the manufacturing of ornamental articles such as jewelry items , watches , watch cases , writing instruments and components of the afore - mentioned goods .
an amorphously solidifying noble metal alloy has the following composition of aabbcc , wherein : a represents at least one noble metal from a group of platinum and palladium ; b represents at least one element from a group of al , au , ag and cu ; and c represents at least one element from a group of ga and ge . the mass fraction a lies in a region of 45 - 60 mass percent . the mass fraction b lies in the region of 39 - 55 mass percent . the mass fraction c lies in the region of 0 - 13 mass percent . where platinum and palladium are both present , the amorphous noble metal alloy does not have aluminum as the sole alloy component from group b . the above mass fractions a , b and c , aside from typical admixtures , impurities and alloy tolerances , add up to 100 mass percent .