as shown in fig1 and 3 , the medical dressings of the present invention includes at least one monolithic , polyurethane foam layer generally designated 1 which is formed by polymerizing an aqueous mixture having one or more hydrocolloid absorptive agents with an aqueous mixture of a hydrophilic polyurethane prepolymer , in a predetermined ratio , so that the polymerization of the polyurethane foam forms a matrix binder for the one or more hydrocolloid absorptive agents . as shown in fig2 the hydrocolloid absorptive agents generally designated 2 are thereby incorporated and integrally dispersed directly into the matrix of the formed foam . the term “ hydrocolloid absorptive agent ” as used in accordance with the present invention includes natural , chemically modified , and synthetic hydrocolloids . suitable hydrocolloids include , but are not limited to , natural gums such as arabic gum , ghatti gum , karaya gum , tragacanth gum , guar gum , locust bean gum and acacia gum ; seaweed extracts such as agar , algin , alginate salts and carrageenin ; cereal gums ; starches ; fermentation or microbial gums such as dextran gum and xanthan gum ; pectins ; gelatins ; casein ; and collagens . modified forms of the hydrocolloids may also be used , including , for example , the oxidized , acetylated , carboxylated , esterified , methylated , aminated , etherated , sulfated , borated and phosphated derivatives of the hydrocolloid absorptive agents . suitable synthetic gums include polyvinylpyrrolidone , low methoxyl pectin , propyleneglycol alginates , carboxymethyl locust bean gum and carboxymethyl guar gum . the medical dressings of the present invention are formed by metering and mixing an aqueous mixture including adequate water and at least one hydrocolloid absorptive agent with a predetermined ratio of hydrophilic urethane prepolymer to provide a prepolymerizing mixture . the hydrocolloid absorptive agents are included in the aqueous phase in an amount of about 0 . 5 % to about 20 . 0 % by weight . more preferably , the hydrocolloid absorptive agents are included in an amount of about 5 % to about 15 % by weight . preferably , the hydrophilic urethane prepolymer is included in the aqueous phase in an amount of about 25 % to about 45 % by weight . suitable surfactants , such as , for example , basf pluronic l 92 or basf pluronic f - 88 ( basf , mt . olive , n . j . ), may preferably be added to the aqueous phase . preferably surfactants may be added in an amount of about 0 . 2 % to about 25 . 0 % wet weight of the aqueous phase . more preferably surfactants may be added in an amount of about 0 . 5 % to about 2 . 5 % wet weight of the aqueous phase . the hydrophilic urethane prepolymer materials used in the medical dressings of the present invention are available in the commercial marketplace , and include , for example , bipol 6 , available from mace adhesives and coatings , and hypol from w . r . grace . general procedures for the preparation and formation of such prepolymers can be found in polyurethanes : chemistry and technology by j . h . saunders and k . c . frisch published by john wiley & amp ; sons , new york , n . y ., at vol . xvi part 2 , high polymer series , “ foam systems ”, pages 7 - 26 , and “ procedures for preparation of polymers ”, pages 26 , et seq ., which are hereby incorporated by reference herein . the medical and wound dressings of the present invention can also include various combinations of other ingredients without departing from the scope of the present invention , including , for example , medicaments , soaps , disinfecting and sterilizing agents , odor management agents , hemostatic agents , proteins , enzymes and nucleic acids . preferably these agents may also be incorporated directly and dispersed throughout the prepolymerization aqueous mixture and are thereby incorporated into the foam matrix . alternatively these other ingredients may be incorporated into the dressing by absorbing them into the formed foam cover layer following the polymerization reaction by affixing to the formed medical and wound dressings , by any suitable means , an additional layer incorporating such other ingredients , as will be understood by those skilled in the art . suitable medicaments , soaps , disinfecting and sterilizing agents , proteins , and enzymes are provided in the commercial market place by a myriad of suppliers and include those which aid recovery of wounds . preferably , the medicaments include antifungal agents , antibacterial agents , angiogenesis promoting agents and the like . more preferred medicaments include antifungal agents such as metronidazole and antibacterial agents such as chlorhexidine . any suitable soap , disinfecting and sterilizing agent may be used . a preferred disinfecting and sterilizing agent includes hydrogen peroxide . suitable proteins and enzymes include those which aid in wound recovery such as fibrin sealants and angiotensins , as described in u . s . pat . nos . 5 , 962 , 420 and 5 , 955 , 430 , hereby incorporated by reference herein . after blending and mixing the combination of the aqueous mixtures and hydrophilic urethane prepolymer , the polymerizing foam composition is preferably deposited on a releasable bottom sheet material on a movable carrier . the upper surface of the polymerizing composition is then covered with a releasable top sheet material and advanced along the moveable carrier for sizing of the foam to the desired thickness and until the foam is tack free . the releasable top and bottom sheets are then sequentially removed . when polymerization is complete , residual water may be driven off by drying the foam . preferably , the drying is done in a drying unit at a temperature of about 200 ° f . drying may also be performed at lower temperatures under reduced pressures . the medical dressings of the present invention may be formed to have any desired thickness or shape . the foam layer is preferably relatively thin . more preferably , the foam layer should have a thickness of about 1 mm to about 10 mm , and more preferably about 1 . 5 mm to about 6 . 0 mm . various forms of the preformed foam medical dressings of the present invention are contemplated . in a preferred embodiment , the medical dressing is an occlusive dressing which includes the foam layer and a biocompatible backing sheet or layer 3 which surrounds the foam layer . any suitable biocompatible backing may be used , however , preferably , the backing is moisture vapor permeable . as shown in fig3 in a preferred embodiment , the backing layer 3 is a hydrophilic polyurethane film which has been laminated to the foam layer 1 . the backing layer 3 may extend beyond the foam layer 1 for contact with the skin of the patient . suitable noncytotoxic and substantially nonallergenic adhesives and / or tapes may be used to apply the medical dressings of the present invention to the skin of a patient . in a preferred embodiment , the adhesive is applied to all or a portion of the backing layer which extends beyond the foam cover layer . preferably , the adhesives and / or tapes include those formed from polymers containing hydrophilic groups , such as hydroxyl , carboxyl , amine , amide , ether and alkoxy . more preferably , the adhesive is a pressure - sensitive acrylic adhesive . such adhesive and tapes are well known in the art and therefore are - not more fully described . it is to be understood that the above - detailed description of the preferred embodiment of the invention is provided by way of example only . various details of the design , construction and composition may be modified without departing from the scope of the invention as set forth in the claims . in addition , the invention will be further described by reference to the following detailed examples . these examples are merely illustrative and not limitative of applicants &# 39 ; invention in any way . an aqueous mixture comprising 4 % karaya gum , water and a suitable surfactant is combined in a 60 : 40 ratio with hydrophilic prepolymer to form the foam . mixing was done at room temperature . l - 92 and f - 88 were added to water and mixed until they were completely dispersed in the water . speed of the mixture was increased and the gum was added slowly into the vortex . mixing was complete when the mixture was smooth ( no gel particles visible ). when mixing was complete , the aqueous was combined with hydrophilic prepolymer as follows the combination was mixed in a high speed mixing vessel until the parts were homogeneous . the combination was then poured and sized using suitable releasable substrate or substrates and allowed to cure until the foam structure was stable . an aqueous mixture comprising 2 % locust bean gum , water and a suitable surfactant was combined in a 60 : 40 ratio with hydrophilic prepolymer to form foam . mixing was done at room temperature . l - 92 and f - 88 were added to the water and mixed until they were completely dispersed in the water . speed of the mixture was increased and the gum was added slowly into the vortex . mixing was complete when the mixture was smooth ( no gel particles visible ). the aqueous was then combined with hydrophilic prepolymer as follows : the combination was mixed in a high speed mixing vessel until the parts were homogeneous . it was then poured and sized using suitable releasable substrate or substrates and allowed to cure until foam structure was stable . comprising 4 % alginate , water and a suitable surfactant was combined in a 60 : 40 ratio with hydrophilic prepolymer to form foam . mixing was done at room temperature . l - 92 and f - 88 were added to the water and mixed until they are completely dispersed in the water . speed of the mixture was increased and the gum was added slowly into the vortex . mixing was complete when the mixture was smooth ( no gel particles visible ). when mixing was complete , the aqueous was combined with hydrophilic prepolymer as follows : the combination was mixed in a high speed mixing vessel until the parts are homogeneous . it was then poured and sized using suitable releasable substrate or substrates and allowed to cure until foam structure is stable . a test was designed to measure the amount of water retained in the foam after squeezing . with the foam containing the hydrocolloid additive , a noticeable increase in the amount of retained water was observed . results of this test using the average of five samples are as follows : results show that standard hydrophilic foam retains about 2 × its own weight and hydrocolloid foam retains 3 × to 8 × its own weight depending on levels of hydrocolloid used .
foam wound dressings for medical and veterinary use are disclosed , along with methods for making the same . the wound dressings contain a hydrophilic polyurethane foam matrix having at least one hydrocolloid absorptive material integrally and generally uniformly dispersed throughout that improves the absorptive properties of the wound dressing . the foam wound dressings are formed from a polymerized combination of an aqueous mixture having at least one hydrocolloid absorptive material with a hydrophilic urethane prepolymer in a predetermined ratio .