referring now to fig1 therein is shown in detail the molding steps of the invention . fig1 shows that a cushion mold 100 is designed with an upper mold portion 102 , which is shaped in the form of the final cushioning pad &# 39 ; s top surface . the mold is then sealed and the cushioning pad compound 104 , which is made of approximately 30 % eva and 70 % tpr by weight , is injected into the mold . the filler agent can be calcium carbonate and can range from about 0 % to about 15 % by weight of the total compound . additionally , the curing agent can be peroxide and can range from about 0 . 4 % to about 1 % by weight of the total compound . the outsole compound can consist of sbs in the range of about 50 % to about 100 % by weight of the rubber and eva in the range of about 45 % to about 60 % by weight of the rubber . additionally , the outsole compound can include a filler and a processing oil . the filler agent can be calcium carbonate or clay and can range from about 2 % to about 7 % by weight of the total compound . the processing oil can be naphthenic or paraffinic based and can range from about 40 % to about 50 % by weight of the total compound . the compound is then allowed to cure . once cured , a fully formed cushioning pad 106 is produced . this cushioning pad 106 is then inserted in a recess 110 in the outsole upper mold 112 . the outsole mold 108 is then sealed and the outsole compound , which is a dry styrene - butadiene - styrene triblock copolymer , ethyl - vinyl - acetate , curing agent , filler agent , blowing agent and a processing oil 114 , is injected into the outsole mold 108 . it is cured to form the outsole / cushioning pad combination 116 . in a preferred embodiment curing agent is peroxide , the filler agent is calcium carbonate , the blowing agent is azodicarbonamide and the processing oil is naphthalene oil . [ 0027 ] fig2 is a flow chart of the process for manufacturing the outsole / cushioning pad combination . first , the compound for the cushion pad is produced by mixing a styrene - butadiene - styrene triblock copolymer ( sbs ), ethyl vinyl acetate ( eva ), curing agent , filler agent , and a blowing agent in a kneader ( step 200 ). then the cushion pad compound is kneaded until well combined . it is then rolled into a sheet approximately 2 . 5 millimeters in thickness ( step 202 ). the cushion pad mold can be heated to a range of temperatures of about 160 ° centigrade to about 180 ° centigrade ( step 204 ). once at the proper temperature , the cushion pad compound is injected into the heated sealed cushion pad mold ( step 206 ). the cushion pad mold is then pressurized to a pressure ranging from about 140 kg / cm 2 to about 160 kg / cm 2 ( step 208 ). the cushion pad should then be cured in the mold at the end of the curing , the fully formed pad is removed from the mold . this cushion pad will typically have a density of about 0 . 2 grams / cm 3 to about 0 . 4 grams / cm 3 ( step 210 ). then the compound for the outsole is mixed by combining a dry styrene - butadiene - styrene triblock copolymer , ethyl - vinyl - acetate , filler , and a processing oil ( step 212 ). next , the cushion pad is placed in a recess in the upper part of the outsole mold 112 ( step 214 ). the outsole compound is then injected into the outsole mold ( step 216 ). lastly , the outsole / cushion pad combination is allowed to cure and then removed from the mold ( step 218 ). [ 0029 ] fig3 is a flow chart illustrating the additional steps to produce an exemplary embodiment of the invention with a planter pad . the method involves repeating steps 200 through 208 in order to form a plantar region pad ( step 300 ). next , the cured plantar region pad is removed the component , for the compound used to form the plantar region are selected so that it has a density greater than the density of the cushion pad . lastly , the plantar region pad may be affixed to the cushion pad prior to the insertion of the cushion pad into the outsole mold step 214 ( step 304 ). referring now to fig4 the completed outsole / cushioning pad is illustrated with the bottom removed to show the interior structure . the tpr outsole 400 is molded around the eva cushioning pad 402 . the eva cushioning pad can be molded to have front trenches or grooves 404 and , cavities 406 that contain other materials . the trenches 404 are formed in the eva cushioning pad 402 and do not reach the tpr outsole 400 . however , the cavities 406 reach down to the material of the outsole bottom 410 . another set of rear hollows 408 can also be molded in the pad . these hollows 408 are just formed in the eva cushioning pad 402 and do not reach down to the tpr outsole 400 . the trenches 404 and cavities 406 are used to add flexibility to the outsole 400 . a portion of an outsole bottom 410 is shown in fig4 . a complete bottom can also be molded to the bottom of the tpr outsole 400 for extra durability . [ 0031 ] fig5 illustrates a cross - section through line 5 - 5 on fig4 . a tpr outsole 400 is molded around the eva cushioning pad 402 . thus , it is not necessary to use glue or adhesives to keep it in place . again , an outsole bottom 410 can also be molded to the bottom of the tpr outsole 400 for extra durability . [ 0032 ] fig6 and 7 illustrate additional cross - sections through lines 6 - 6 and 7 - 7 respectfully on fig4 . a tpr outsole 400 is molded around the eva cushinong pad 402 . fig6 illustrates the rear hollows 408 and that the hollows 408 do not go to the bottom of the eva pad 402 . however , the cavities 406 illustrated in fig7 are molded so they penetrate completly through the eva pad 402 and extend down to the material of the outsole bottom 410 . referring to fig8 here is illustrated a cross - section through the plantar region of the shoe . in an exemplary embodiment , a plantar region pad 800 is affixed to the bottom of the cushion pad 402 and extends to the outsole bottom 410 . this plantar region pad 800 may be of a different density then the cushion pad 402 . typically , the plantar region pad 800 will have a greater density to provide more support . [ 0034 ] fig9 illustrates an exploded perspective view of the shoe of the present invention . the shoe is comprised of a cushion pad 900 , an outsole 902 and an upper 904 . the outsole 902 also has a bottom 906 . the cushion pad 900 is formed , either with or without an additional plantar region pad 910 . once formed , the cushion pad 900 is then molded to the outsole 902 . this acts as if the outsole pad 900 is placed in a cavity 908 in the outsole 902 , but it is actually formed inside for improved qualities as discussed above . the cushion pad compound includes sbs in the range of about 50 to about 100 parts per hundred parts of rubber (“ phr ”). to equate to a full 100 parts of rubber , eva can be added in the range of about 0 phr to about 50 phr . the exemplary embodiment contains 70 % by weight of sbs an 30 % by weight of eva wherein the eva itself includes about 15 % to about 18 % vinyl acetate . additionally , additives may be required to be added to the rubber to give it all of the properties of the current invention . peroxide , a curing agent , may be added in the range of about 0 . 5 to about 1 . 0 phr . also , calcium carbonate , a filler agent , may be added in the range of about 0 to about 10 phr . lastly , azodicarbonamide , a blowing agent , may be added in the range of about 3 to about 5 phr . a second portion of a shoe is the outsole and the exemplary embodiment of the outsole composition is again sbs in the range of about 50 to about 100 phr and eva in the range of about 45 to about 60 phr . the additives for this compound may include naphthenic oils , a processing oil , may be added in the range of about 80 to about 120 phr . lastly , calcium carbonate , a filler agent , may be added in the range of about 5 to about 15 phr . thus , while there have been shown , described , and pointed out fundamental novel features of the invention as applied to a preferred embodiment thereof , it will be understood that various omissions , substitutions , and changes in the form and details of the devices illustrated , and in their operation , may be made by those skilled in the art without departing from the spirit and scope of the invention . for example , it is expressly intended that all combinations of those elements and / or steps which perform substantially the same function , in substantially the same way , to achieve the same results are within the scope of the invention . substitutions of elements from one described embodiment to another are also fully intended and contemplated . it is also to be understood that the drawings are not necessarily drawn to scale , but that they are merely conceptual in nature . it is the intention , therefore , to be limited only as indicated by the scope of the claims appended hereto .
the present invention discloses a compound and a method for a cushion pad that is bonded to an outsole without the need for glue or other adhesives . this cushion pad can be softer and more flexible then the outsole but can be similar enough in composition to be recyclable without having to separate it from the outsole . the compound can consist of a styrene - butadiene - styrene triblock copolymer , ethyl - vinyl - acetate , peroxide , a filler agent , and a blowing agent . the combination of these materials will form a high rubber content foam sheet that is very soft and shock adsorbing . this process can use the above compound to manufacture a rubber outsole with an integrated cushioning pad that can be manufactured in one step .