referring to fig1 , basic steps in the method of making the matrix of the present invention are illustrated . in a first step at block 10 , preferably , a pure stock of a milo grain is selected . although there is no specific hybrid of milo which is required for the product and method of the present invention , it is desirable to choose a single pure stock grain because this pure stock grain is advantageous in creating consistency and repeatability of the extrusion process . through testing , it has been found that a few particular hybrids of milo are particularly adapted for extrusion . three hybrid varieties which have shown great success include triumph 65g , asgrow seneca ; and dekalb 5400 . these three hybrid varieties are well known grain stocks for use in animal feed , and are commercially available in the u . s . although these three hybrids are preferred , it shall be understood that there may be a number of other hybrid varieties of milo which are also adapted for consistent and repeatable extrusion . the next step in the process shown at block 12 is to clean and size the milo grain . standard cleaning and sizing equipment may be used to process the grain at this step . for example , air / water streams may be used to clean the grain , and the grain may be passed through various sieves to obtain the desired grain size . in the present invention however , there is no particular grain size required and multiple grain sizes may be used . shown at block 14 is the next step in the process which is an optional destoning operation to remove stones or other similar sized objects which may still remain in the grain after cleaning and sizing . although a destoning operation is shown as a separate optional step , destoning can be incorporated within the cleaning and sizing of the grain at step 12 . the next step in the process is shown at block 16 which is the decortication of the milo grain . anyone of several methods of usual grain decortication may be used to decorticate the milo . two references which disclose methods for decorticating milo and which have been found to be particularly effective are the methods described in the u . s . pat . nos . 5 , 713 , 526 and 5 , 820 , 039 . these two references are incorporated herein by reference for purposes of disclosing basic methods by which milo grain may be decorticated . the next step in the method is shown at block 18 which is an optional step of scouring the grain to remove fatty oils or lipids . in order to enhance the consistency and repeatability of the extrusion process , the fatty endogerm of the milo may be removed because this fatty portion of the grain tends to act as a lubricant through the extrusion die thereby degrading extruder operation . well known grain scouring processes may be used to remove the fatty endogerm from the milo grain . although scouring is discussed as a step in the basic method , it shall be understood that scouring is not necessarily required as it may be desirable to have certain levels of fat within the matrix . additionally , scouring may be eliminated to simplify the overall production process . the next step in the method is shown at block 20 which involves the introduction of a desired anti - fungal / anti - microbial agent to the processed milo . the milo combined with the anti - fungal / anti - microbial agent are referred to as a grain mix . there are a number of anti - fungal / anti - microbial agents which are contemplated within the present invention which may be used for inhibiting mold growth , or inhibiting growth of microbes . many naturally occurring plant products have been identified that possess significant anti - fungal and anti - bacterial activity . for example , the terpenes are isomeric hydrocarbons found primarily in essential oils , resins and balsams that possess strong anti - fungal activity . thus , terpenes and especially y - terpinene , terpinolene , terpinen - 4 - ol , as well as 1 , 8 - cineole , p - cymene and pinene are preferred anti - fungal agents for use in the construction materials of the present invention . additionally , phytoalexins found in sorghum are induced after the plant is exposed to fungal pathogens . the most active phytoalexins include apigeninidin , luteolinidin , a caffeic acid ester of arabinosyl - 5 - o - apigeninidin , and 5 - methoxy - luteolinidin . thus , these natural mold inhibitors are found within the milo grain itself . for example , in red milo , the major pigments found in the hulls of this sorghum are apigeninidin and luteolinidin . therefore , it is also contemplated within the present invention to recover the hulls of the grain which are removed during decortication and then process the hulls to extract the apigeninidin and luteolinidin . these removed pigments can then be added back to the decorticated grain prior to extrusion and used as the anti - fungal agents . calcium propionate is another compound known to have significant anti - fungal activity and is compatible with the naturally occurring plant products listed above . thus , the construction materials of the present invention include an extruded milo matrix incorporating anti - fungal compounds including calcium propionate , at least one terpene and at least one phytoalexin . preferably , the construction material incorporates at least one of calcium propionate , apigeninidin , luteolinidin , a caffeic acid ester of arabinosyl - 5 - o - apigeninidin , 5 - methoxy - luteolinidin , y - terpinene , terpinolene , terpinen - 4 - ol , 1 , 8 - cineole , p - cymene and / or pinene in an extruded milo matrix . depending on the intended use and storage conditions of the construction material each of these individual ingredients may be included in an amount of between about 0 % to about 50 % on a weight / weight basis in the extruded milo matrix . that is , each of the individual ingredients listed above may be absent or may be present in a concentration as high as 50 % w / w of the extruded milo matrix . particularly preferred embodiments of the present invention are described in table 1 which lists the amounts of the active and inactive ingredients in the construction materials . the inactive ingredients represent the extruded milo matrix which includes amylose - pectin starch , calcium , potassium , phosphorus , sulfur , manganese and ash . the water content of the material , if any , is not shown in table 1 . in order to provide an extrudable mixture , it is preferable to maintain the milo at or around 16 % moisture content prior to extrusion . accordingly , an amount of water must be added to the decorticated milo prior to extrusion . depending upon the type of agent which is added to the decorticated milo , a lesser or greater amount of water must be added to bring the moisture content of the milo grain mix to preferably around 16 % moisture . it may be desirable to mechanically mix the grain mix in a bin which will then meter the grain mix into the extrusion machine . mechanical mixing helps to ensure uniform dispersion of the added agent . the next step in the method is illustrated at block 22 which involves extrusion of the milo grain mix . through testing , it has been found that extrusion can be achieved utilizing a bake - type extruder which exposes the grain mix to heat in the range of about 325 ° f . to about 400 ° f . and pressure in the range of between about 1500 and about 2000 psi . the particular shape of the die used in the extruding machine may be adapted to produce a matrix of a desired shape . one example is a die having a round shaped hole with a diameter of approximately 0 . 120 of an inch . the cutting mechanism used in the extruding machine could be adapted for cutting the extrudate to a length of approximately three - quarters of an inch . the resulting extruded product can be of different sizes and densities . for example , if a particularly small enclosed space must be remediated by introduction of the matrix , it may be desirable to provide the matrix in a more dense extrudate . accordingly , the extrudate could have a smaller size and a nugget - like consistency . if the area to be remediated had not yet developed fungal or microbial problems and the purpose of introducing the matrix was primarily for prevention , then it may be adequate to provide the matrix in a larger sized , lighter , puffier extrudate . the amount of the anti - fungal / anti - microbial agent in the denser , nugget - like extrudate would be greater since more matrix is used per piece of extrudate while the amount of the anti - fungal / antimicrobial agent would be more dispersed within the lighter , puffy extrudate . since the concentration of the anti - fungal / antimicrobial agent can vary depending upon the density of the extrudate , the extrudate can be tailored for each application . of course , one could also simply vary the amount of the agent used when it is initially mixed with the decorticated milo to provide the desired concentration of the agent in the matrix . the last step of the method is shown at block 24 which contemplates curing the matrix product to thereby stabilize the product prior to storage and shipping . depending upon the matrix produced , i . e ., one which is either puffed or more dense , a certain amount of curing may be required to allow the matrix to reach equilibrium in terms of moisture content . there are a number of advantages of utilizing a milo matrix as a carrier for an anti - fungal and / or anti - microbial agent . first , the extruded milo is naturally hydrophobic which therefore allows the milo matrix to be used in damp or wet spaces for extended periods of time without substantial decay . milo is a readily available grain source , and is relatively inexpensive compared to man made or artificial compositions . another advantage as mentioned above is the ability to produce a matrix which has a variety of sizes and densities by simply altering the moisture content of the grain mix prior to extrusion . by altering the density , the concentration of the agent may also be adjusted . after extrusion , the milo matrix contains some percentage of carbohydrates ; however , the matrix is very low in nutritional value , and has little odor . the matrix has no detectable amounts of sugars , less than 2 % fat and less than 10 % protein . therefore , the matrix does not attract rodents or insects . the matrix of the present invention is easily deployed within many commercial structures by simply transporting the matrix to a desired location , and spreading the matrix within the desired space to be remediated or for prevention of mold and / or microbial growth . for prevention of mold , it has been found that spreading a layer of 3 - 6 inches of the lighter , puffier , matrix over the targeted area is adequate for preventing mold growth . for remediation of mold , it may be necessary to increase the depth of the spread matrix , and it may also be necessary to increase the density of the matrix at a particular location . as best understood , there are two primary ways in which the agent inhibits mold or microbial growth . the first is physical contact of the matrix with the area to be remediated . the second is production of an off - gas through sublimation of the additive into the atmosphere enclosed by the space to be remediated . for example , with chlorine , a certain amount of the solid chlorine will off - gas producing a vapor which prevents mold growth . of course , the concentration of the chlorine in the milo matrix has to be controlled so that the off gas produced does not reach dangerous levels . it may be necessary over time to add additional amounts of the matrix to the area to be remediated . as the agent continues to sublime or otherwise chemically break down , the concentration of the agent will diminish . the present invention has been described with respect to a preferred embodiment however , other changes and modifications may be made to the invention within the spirit and scope thereof .
the invention provides a composition useful in the construction industry for the prevention or remediation of mold growth in a man made structure . the composition contains an extruded milo matrix incorporating terpenes , phytoalexins , calcium propionate or combinations of these chemicals having antifungal activity . methods of making and using the compositions are also disclosed .