the present invention relates to a method for making an intravascular stent . the underlying structure of the stent can be virtually any stent design , whether of the self - expanding type or of the balloon - expandable type and whether metal or polymeric . thus metal stent designs such as those disclosed in u . s . pat . no . 4 , 733 , 665 issued to palmaz , u . s . pat . no . 4 , 800 , 882 issued to gianturco or u . s . pat . no . 4 , 886 , 062 issued to wiktor could be used in the present invention . for example , the configuration of the stent 1 shown in fig3 is such , that a wire has a reversing bend pattern 2 so that controlled radial expansion of the stent 1 is accomplished by the force generated by an inflating balloon 3 . when acted upon by the inflating balloon 3 , the stent 1 expands radially by controlled deformation and tension applied to the pattern 2 of the wire . the expanded larger diameter will conform to the inside of the vessel 4 and maintain intimate contact with the inside wall due to the low memory level of the deformable metal used for the wire . the stent could be made of virtually any bio - compatible material having physical properties suitable for the design . for example , tantalum and stainless steel have been proven suitable for many such designs and could be used in the present invention . also , stents made with biostable or bioabsorbable polymers such as poly ( ethylene terephthalate ), polyacetal , poly ( lactic acid ), poly ( ethylene oxide )/ poly ( butylene terephthalate ) copolymer could be used in the present invention . although the stent surface should be clean and free from contaminants that may be introduced during manufacturing , the stent surface requires no particular surface treatment in order to retain the coating applied in the present invention . both the inner and outer surfaces of the stent may be provided with the coating according to the present invention . in order to provide the coated stent according to the present invention , a solution which includes a solvent , a polymer dissolved in the solvent and a therapeutic substance dispersed in the solvent is first prepared . it is important to choose a solvent , a polymer and a therapeutic substance that are mutually compatible . it is essential that the solvent is capable of placing the polymer into solution at the concentration desired in the solution . it is also essential that the solvent and polymer chosen do not chemically alter the therapeutic character of the therapeutic substance . however , the therapeutic substance only needs to be dispersed throughout the solvent so that it may be either in a true solution with the solvent or dispersed in fine particles in the solvent . examples of some suitable combinations of polymer , solvent and therapeutic substance are set forth in table 1 below . table 1______________________________________polymer solvent therapeutic substance______________________________________poly ( l - lactic chloroform dexamethasoneacid ) poly ( lactic acetone dexamethasoneacid - co - glycolic acid ) polyether n - methyl tocopherolurethane pyrrolidone ( vitamin e ) silicone xylene dexamethasoneadhesive phosphatepoly ( hydroxy - dichloro - aspirinbutyrate - co - methanehydroxyvalerate ) fibrin water heparin ( buffered saline ) ______________________________________ the solution is applied to the stent and the solvent is allowed to evaporate , thereby leaving on the stent surface a coating of the polymer and the therapeutic substance . typically , the solution can be applied to the stent by either spraying the solution onto the stent or immersing the stent in the solution . whether one chooses application by immersion or application by spraying depends principally on the viscosity and surface tension of the solution , however , it has been found that spraying in a fine spray such as that available from an airbrush will provide a coating with the greatest uniformity and will provide the greatest control over the amount of coating material to be applied to the stent . in either a coating applied by spraying or by immersion , multiple application steps are generally desirable to provide improved coating uniformity and improved control over the amount of therapeutic substance to be applied to the stent . the polymer chosen must be a polymer that is biocompatible and minimizes irritation to the vessel wall when the stent is implanted . the polymer may be either a biostable or a bioabsorbable polymer depending on the desired rate of release or the desired degree of polymer stability , but a bioabsorbable polymer is probably more desirable since , unlike a biostable polymer , it will not be present long after implantation to cause any adverse , chronic local response . bioabsorbable polymers that could be used include poly ( l - lactic acid ), polycaprolactone , poly ( lactide - co - glycolide ), poly ( hydroxybutyrate ), poly ( hydroxybutyrate - co - valerate ), polydioxanone , polyorthoester , polyanhydride , poly ( glycolic acid ), poly ( d , l - lactic acid ), poly ( glycolic acid - co - trimethylene carbonate ), polyphosphoester , polyphosphoester urethane , poly ( amino acids ), cyanoacrylates , poly ( trimethylene carbonate ), poly ( iminocarbonate ), copoly ( ether - esters ) ( e . g . peo / pla ), polyalkylene oxalates , polyphosphazenes and biomolecules such as fibrin , fibrinogen , cellulose , starch , collagen and hyaluronic acid . also , biostable polymers with a relatively low chronic tissue response such as polyurethanes , silicones , and polyesters could be used and other polymers could also be used if they can be dissolved and cured or polymerized on the stent such as polyolefins , polyisobutylene and ethylene - alphaolefin copolymers ; acrylic polymers and copolymers , vinyl halide polymers and copolymers , such as polyvinyl chloride ; polyvinyl ethers , such as polyvinyl methyl ether ; polyvinylidene halides , such as polyvinylidene fluoride and polyvinylidene chloride ; polyacrylonitrile , polyvinyl ketones ; polyvinyl aromatics , such as polystyrene , polyvinyl esters , such as polyvinyl acetate ; copolymers of vinyl monomers with each other and olefins , such as ethylene - methyl methacrylate copolymers , acrylonitrile - styrene copolymers , abs resins , and ethylene - vinyl acetate copolymers ; polyamides , such as nylon 66 and polycaprolactam ; alkyd resins ; polycarbonates ; polyoxymethylenes ; polyimides ; polyethers ; epoxy resins , polyurethanes ; rayon ; rayon - triacetate ; cellulose , cellulose acetate , cellulose butyrate ; cellulose acetate butyrate ; cellophane ; cellulose nitrate ; cellulose propionate ; cellulose ethers ; and carboxymethyl cellulose . the ratio of therapeutic substance to polymer in the solution will depend on the efficacy of the polymer in securing the therapeutic substance onto the stent and the rate at which the coating is to release the therapeutic substance to the tissue of the blood vessel . more polymer may be needed if it has relatively poor efficacy in retaining the therapeutic substance on the stent and more polymer may be needed in order to provide an elution matrix that limits the elution of a very soluble therapeutic substance . a wide ratio of therapeutic substance to polymer could therefore be appropriate and could range from about 10 : 1 to about 1 : 100 . the therapeutic substance used in the present invention could be virtually any therapeutic substance which possesses desirable therapeutic characteristics for application to a blood vessel . this can include both solid substances and liquid substances . for example , glucocorticoids ( e . g . dexamethasone , betamethasone ), heparin , hirudin , tocopherol , angiopeptin , aspirin , ace inhibitors , growth factors , oligonucleotides , and , more generally , antiplatelet agents , anticoagulant agents , antimitotic agents , antioxidants , antimetabolite agents , and anti - inflammatory agents could be used . antiplatelet agents can include drugs such as aspirin and dipyridamole . aspirin is classified as an analgesic , antipyretic , anti - inflammatory and antiplatelet drug . dypridimole is a drug similar to aspirin in that it has anti - platelet characteristics . dypridimole is also classified as a coronary vasodilator . anticoagulant agents can include drugs such as heparin , coumadin , protamine , hirudin and tick anticoagulant protein . antimitotic agents and antimetabolite agents can include drugs such as methotrexate , azathioprine , vincristine , vinblastine , fluorouracil , adriamycin and mutamycin . a 1 % solution of dexamethasone in acetone was made , forming a clear solution . the solution was placed in an airbrush reservoir ( badger # 200 ). wiktor type tantalum wire stents were sprayed with the solution in short bursts while rotating the stents . the acetone quickly evaporated from the stents , leaving a white residue on the stent wire . the process was continued until all of the stent wires were coated . the drug elution rate for the stent was determined by immersing the stent in phosphate buffered saline solution ( ph = 7 . 4 ). traces of dexamethasone were observed to remain on the immersed stents for less than 31 hours . a 2 % solution of dexamethasone in acetone was made , forming a solution with suspended particles of dexamethasone . the solution was placed into a tube . wiktor type tantalum wire stents were dipped rapidly and were allowed to dry . each stent was dipped into the solution 12 - 15 times to provide a white surface coating . two stents were placed on an angioplasty balloon and were inflated on the balloon . approximately 80 % of the dexamethasone coating flaked off of the stents . a solution of 1 % dexamethasone and 0 . 5 % poly ( caprolactone ) ( aldrich 18 , 160 - 9 ) in acetone was made . the solution was placed into a tube . wiktor type tantalum wire stents were dipped rapidly and were allowed to dry . each stent was dipped into the solution 12 - 15 times to provide a white surface coating . a stent so coated was expanded on a 3 . 5 mm angioplasty balloon causing a significant amount of the coating to become detached . a solution of 1 % dexamethasone and 0 . 5 % poly ( l - lactic acid ) ( medisorb ) in acetone was made . the solution was placed into a tube . wiktor type tantalum wire stents were dipped rapidly and were allowed to dry . each stent was dipped into the solution 12 - 15 times to provide a white surface coating . a stent so coated was expanded on a 3 . 5 mm angioplasty balloon causing only a small portion of the coating ( less than 25 %) to become detached ) a solution including a 2 % dispersion of dexamethasone and a 1 % solution of poly ( l - lactic acid ) ( cca biochem mw = 550 , 000 ) in chloroform was made . the solution was placed into an airbrush ( badger ). wiktor type tantalum wire stents were sprayed in short bursts and were allowed to dry . each stent was sprayed with the solution about 20 times to provide a white surface coating . a stent so coated was expanded on a 3 . 5 mm angioplasty balloon . the coating remained attached to the stent throughout the procedure . a solution including a 2 % dispersion of dexamethasone and a 1 % solution of poly ( l - lactic acid ) ( cca biochem mw = 550 , 000 ) in chloroform was made . the solution was placed into an airbrush ( badger # 250 - 2 ). wiktor type tantalum wire stents were suspended from a fixture and sprayed in 24 short bursts ( 6 bursts from each of the four directions perpendicular to the stent axis ) and were allowed to dry . the resulting stents had a coating weight of about 0 . 0006 - 0 . 0015 grams . three of the stents were tested for long term elution by placing one stent in 3 . 0 ml of phosphate buffered saline solution ( ph = 7 . 4 ) at room temperature without stirring . the amount of dexamethasone eluted was evaluated by measuring absorbance at 244 nm in a uv - vis spectrophotometer . the results of this test are given in fig1 . a solution including a 2 % dispersion of dexamethasone and a 1 % solution of poly ( l - lactic acid ) ( medisorb 100 - l ) in chloroform was made along with a control solution of 1 % of poly ( l - lactic acid ) ( medisorb 100 - l ) in chloroform . the solutions was placed into an airbrush ( badger # 250 - 2 ). wiktor type tantalum wire stents were expanded on a 3 . 0 mm balloon , suspended from a fixture and sprayed in 16 short bursts ( 2 - 3 bursts of about 1 second followed by several minutes drying time between applications ). the resulting dexamethasone - coated stents had an average coating weight of about 0 . 0012 grams while the polymer - coated stents had an average polymer weight of about 0 . 0004 grams . the stents were sterilized in ethylene oxide . three of the sterilized dexamethasone - coated stents were tested for long term elution by placing one stent in 3 . 0 ml of phosphate buffered saline solution ( ph = 7 . 4 ) at room temperature without stirring . the amount of dexamethasone eluted was evaluated by measuring absorbance at 244 nm in a uv - vis spectrophotometer . the results of this test are given in fig2 . dexamethasone - coated stents and polymer - coated control stents were implanted in the coronary arteries of 8 pigs ( n = 12 for each type ) according to the method set forth in &# 34 ; restenosis after balloon angioplasty -- a practical proliferative model in porcine coronary arteries ,&# 34 ; by robert s . schwartz , et al , circulation 82 ( 6 ): 2190 - 2200 , december 1990 , and &# 34 ; restenosis and the proportional neointimal response to coronary artery injury : results in a porcine model &# 34 ; by robert s . schwartz et al , j am coll cardiol ; 19 ; 267 - 74 february 1992 with the result that when compared with the controls , the dexamethasone - coated stents reduced the amount of proliferation associated with the arterial injury . it will be appreciated by those skilled in the art that while the invention has been described above in connection with particular embodiments and examples , the invention is not necessarily so limited and that numerous other embodiments , examples , uses , modifications and departures from the embodiments , examples and uses may be made without departing from the inventive concepts .
a method for making an intravascular stent by applying to the body of a stent a solution which includes a solvent , a polymer dissolved in the solvent and a therapeutic substance dispersed in the solvent and then evaporating the solvent . the inclusion of a polymer in intimate contact with a drug on the stent allows the drug to be retained on the stent during expansion of the stent and also controls the administration of drug following implantation . the adhesion of the coating and the rate at which the drug is delivered can be controlled by the selection of an appropriate bioabsorbable or biostable polymer and the ratio of drug to polymer in the solution . by this method , drugs such as dexamethasone can be applied to a stent , retained on a stent during expansion of the stent and elute at a controlled rate .