Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component.
In a prospective randomized controlled trial (RCT), we assessed polyethylene wear and acetabular component stability (primary outcome) with radiostereometric analysis (RSA) in 68 patients with reverse hybrid THA at five years follow-up. Patients were randomized to either a VEPE or a ModXLPE cemented acetabular component.
Mean polyethylene wear in the proximal direction was 0.17 mm (SD 0.15) for the VEPE group and 0.20 mm (SD 0.09) for the ModXLPE group (p = 0.005) at five years. Annual proximal wear rates were 0.03 mm/year (VEPE) and 0.04 mm/year (ModXLPE). Total 3D wear was 0.21 mm (SD 0.26) and 0.23 mm (SD 0.10) for the VEPE and ModXLPE groups, respectively (p = 0.009). Total 3D cup translation was 0.72 mm (SD 0.70) (VEPE) and 0.50 mm (SD 0.44) (ModXLPE) (p = 0.409).
At five years, there was less polyethylene wear in the VEPE group than in the ModXLPE group. Both VEPE and ModXLPE cemented components showed low annual wear rates. Component stability was similar in the two groups and remained constant up to five years. Whether these results will equate to a lower long-term revision rate is still unknown. Cite this article: 