A microstructural study of the thermal fatigue failures of 60sn-40Pb solder joints
When an electronic package encounters thermal fluctuations, cyclical shear strain is imposed on the solder joint interconnections. The thermal cycling leads to a condition of thermal fatigue and eventual solder joint failure. This study was performed in order to understand the microstructural mechanisms that lead to solder joint failures in thermal fatigue. Thermal cycling tests were performed on 60Sn-40Pb joints using a -55° C to 125° C cycle and 19% imposed shear strain. A heterogeneously coarsened region of both Pb and Sn-rich phases develops within the 60Sn-40Pb solder joints. Cracks initiate in the heterogeneously coarsened Sn-rich phase at the Sn-Sn grain boundaries. Heterogeneous coarsening and failure occurs in both high (35 to 125° C) and low (-55 to 35° C) thermal cycles. The elevated temperature portion of the thermal cycle was found to be the most significant factor in the heterogeneous coarsening and failure of the solder joints.