Kinetics of crystal nucleation of poly(L-lactic acid)
Abstract The kinetics of crystal nucleation of poly(L-lactic acid) (PLLA) has been analyzed by fast scanning chip calorimetry in a wide temperature range between 313 and 383 K, that is, between temperatures about 30 K below and 40 K above the glass transition temperature. The relaxed melt was rapidly cooled to the analysis temperature and subsequently aged between 10 −1 and 10 4  s, to permit formation of nuclei. The number of formed crystal nuclei has been probed by analysis of the crystallization rate at 393 K. The nucleation rate is maximal at 370–375 K and decreases monotonously with decreasing temperature in the analyzed temperature range. The observation of a monomodal dependence of the nucleation rate on temperature points to predominance of a single nucleation mechanism in the analyzed temperature range, regardless nucleation occurs in the glassy or devitrified amorphous phase. The collected data suggest that nuclei formation at ambient temperature requires a waiting time longer than about 10 8  s. The performed study is considered as a quantitative completion of nucleation-rate data available for PLLA only at temperatures higher than 360 K, suggesting that the nucleation mechanism is independent on temperature in the analyzed temperature range between 313 and 383 K.