Fracture behavior of metal oxide/silver nanowire composite electrodes under cyclic bending
Abstract The mechanical responses under cyclic bending of Ag nanowire composite electrodes coated with various metal oxide films of different thicknesses were explored, in an attempt to evaluate their applicability to flexible transparent electrodes. Al 2 O 3 , HfO 2 , and TiO 2 films were deposited onto Ag nanowire electrodes by atomic layer deposition at a low temperature of 100 °C, and cyclic bending tests with in situ resistance measurements were conducted for up to 300,000 cycles. Thicker metal oxide films resulted in greater increases in the resistances of the composite electrodes under cyclic bending due to the reduced fracture strength of the films. Regardless of the type of metal oxide, however, similar tendencies were observed in the resistance changes in response to cyclic bending. It was found that the critical thickness calculation based on the Griffith theory for the evaluation of the brittle-to-ductile transition was not applicable to the metal oxide/Ag nanowire composite electrodes. By correlating the mechanical, ambient, and thermal reliability test results with those of optoelectrical property evaluations, the optimal thickness of Al 2 O 3 film, as a representative metal oxide film, was determined to be 3–5 nm for Ag nanowire composite flexible transparent electrodes.