The present invention relates to a reversibly thermochromic light-shielding/light-transmitting laminate member. More particularly, the invention relates to a reversibly thermochromic light-shielding/light-transmitting laminate member, which changes not only in color but in transmittance with temperature.
A laminate member which undergoes alternate color changes between a colorless transparent state and a colored opaque state with temperature is disclosed in U.S. Pat. No. 5,490,956. This laminate member comprises a substrate and formed thereon a reversibly thermochromic layer comprising a vinyl chloride/vinyl acetate copolymer resin matrix and dispersed therein a reversibly thermochromic composition comprising (a) an electron-donating color-forming organic compound, (b) an electron-accepting compound, and (c) a reaction medium determining the temperatures at which the color reactions of component (a) with component (b) take place.
The thermochromic composition contained in the reversibly thermochromic layer is not encapsulated, i.e., of the so-called non-capsule type. Because of this, not only the thermochromic layer has a factor contributing to chemical instability, but also the substrate is limited in material. With respect to thermochromic properties, the laminate member has such color-memorizing properties that it is wide hysteretic and memorizes and retains a color-changed state resulting from a temperature change.
An aim of the invention is to eliminate the drawbacks of the known reversibly thermochromic laminate member which undergoes alternate color changes between a colorless transparent state and a colored opaque state. Namely, the aim is to provide a reversibly thermochromic light-shielding/light-transmitting laminate member which has a satisfactory thermochromic function and is free from the factor contributing to chemical instability inherent in the system employing a non-capsule type reversibly thermochromic composition.
The invention provides a reversibly thermochromic light-shielding/light-transmitting laminate member which comprises a substrate and formed thereon a reversibly thermochromic layer comprising a transparent resin and fixedly dispersed therein a reversibly thermochromic microencapsulated pigment containing a reversibly thermochromic composition comprising (a) an electron-donating color-forming organic compound, (b) an electron-accepting compound, and (c) a reaction medium determining the temperatures at which the color reactions of component (a) with component (b) take place, the reversibly thermochromic microencapsulated pigment being a deformable pigment which has an average particle diameter of from 0.1 to 5.0 xcexcm, the transparent resin having a tensile elongation at break of 350% or lower. In the laminate member of the invention, the proportion of the reversibly thermochromic microencapsulated pigment to the transparent resin is preferably from 1/0.5 to 1/20 (in terms of weight ratio on a solid basis) and the reversibly thermochromic layer preferably has a thickness of from 5 to 100 xcexcm. Furthermore, the transparent resin is preferably a resin selected from the group consisting of methyl methacrylate resins, acrylic resins, vinyl chloride/vinyl acetate copolymer resins, ethylene/vinyl acetate copolymer resins, saturated polyester resins, unsaturated polyester resins, butyral resins, polyurethane resins, polyamide resins, styrene resins, acrylic/styrene resins, ketone resins, and epoxy resins. In one embodiment of the invention, the laminate member has, formed over the reversibly thermochromic layer, a metallic glossy layer containing a metallic luster pigment having transparency. This metallic glossy layer preferably has a light transmittance of 5% or higher.
The laminate member of the invention, which undergoes alternate color changes between a colorless transparent state and a colored opaque state with temperature, is obtained based on a combination of a reversibly thermochromic microencapsulated pigment having an average particle diameter of from 0.1 to 5.0 xcexcm with a transparent resin having a tensile elongation at break of 350% or lower, as stated above.
More particularly, the reversibly thermochromic layer comprising a combination of a reversibly thermochromic microencapsulated pigment having an average particle diameter of from 0.1 to 5.0 xcexcm with a transparent resin having a tensile elongation at break of 350% or lower is presumed to undergo the following phenomena.
The microencapsulated pigment has different capsule shapes depending on whether the reversibly thermochromic composition contained therein is in a solid state, i.e., a colored state, or is in a dissolved state, i.e., a decolored state. Specifically, when the encapsulated composition is in a dissolved state (decolored state), then the capsules have a degree of freedom and are deformable because the reversibly thermochromic composition is liquid. However, when the encapsulated composition is in a solid state (colored state), the capsules have recesses in the surface thereof, which were formed upon solidification of the reversibly thermochromic composition, and are hard and less apt to be deformed.
On the other hand, the transparent resin used in the invention has an elongation as low as 350% or below and does not conform to capsule shape changes with temperature. In addition, the microencapsulated pigment is kept fixed while retaining a given shape. From these, the following can be presumed. When the encapsulated reversibly thermochromic composition is in a dissolved state (decolored state), the capsules have a degree of freedom in shape change and are dispersed while in close contact with the surrounding transparent resin. However, when the reversibly thermochromic composition is in a solid state (colored state), the capsules have recesses in the surface thereof, resulting in spaces between the capsules and the transparent resin which has been in close contact therewith or resulting in spaces inside the capsules. This change in combination with color changes produces the following effects. When the reversibly thermochromic composition is in a solid state, the reversibly thermochromic layer is in a colored state and is opaque due to a bleaching phenomenon caused by light scattering by the spaces. When the reversibly thermochromic composition is in a dissolved state, the reversibly thermochromic layer is in a decolored state and is transparent because the light-scattering phenomenon attributable to the spaces does not occur since the capsules are in close contact with the transparent resin.
Requirements for enabling the color changes to occur include the particle diameter of the capsules which is regulated to 0.1 to 5.0 xcexcm. The reasons for this are as follows. In case where the particle diameter of the capsules is smaller than 0.1 xcexcm, not only satisfactory thermochromic properties cannot be obtained, but also such capsules should have a reduced wall thickness and hence have poor durability in secondary processing, making it difficult to satisfy suitability for practical use. In case where the particle diameter thereof exceeds 5.0 xcexcm, the microencapsulated pigment itself has considerably reduced light transmission and, hence, the reversibly thermochromic layer in a decolored state has reduced light transmission. The particle diameter of the capsules is preferably from 0.3 to 3.0 xcexcm, more preferably from 0.5 to 2.0 xcexcm. Use of such capsules enables the reversibly thermochromic layer to show transparency and a sufficient color density in a colored state, be reduced in a residual color in a decolored state, and have excellent sharpness in color change. Namely, the reversibly thermochromic layer can have an excellent balance among thermochromic functions.
As described above, the invention is based on such an epoch-making technique that light transmission in a decolored state and opacity (hiding properties) in a colored state are attained respectively by using capsules having a reduced particle size and by using a combination of a transparent resin having a tensile elongation at break of 350% or lower with a microencapsulated pigment which is deformable.
The proportion of the microencapsulated pigment to the transparent resin in terms of weight ratio on a solid basis is preferably from 1/0.5 to 1/20, more preferably from 1/1 to 1/10. The thickness of the reversibly thermochromic layer is preferably from 5 to 100 xcexcm, more preferably from 30 to 60 xcexcm.
In case where the proportion of the microencapsulated pigment to the transparent resin in terms of weight ratio on a solid basis exceeds 1/0.5, the pigment content is so high that transparency is reduced and the reversibly thermochromic coating layer has a reduced strength. In case where the proportion thereof is lower than 1/20, i.e., the proportion of the transparent resin exceeds the upper limit, then an excessively large film thickness is necessary for obtaining a satisfactory color density and this leads to insufficient drying and to problems concerning coating period, etc. Thus, such too high proportions of the transparent resin are unsuitable for practical use.
Thicknesses of the reversibly thermochromic layer smaller than 5 xcexcm result not only in difficulties in obtaining a satisfactory color tone in a colored state but also in poor hiding properties. On the other hand, thicknesses thereof exceeding 100 xcexcm may impair the transparency of the layer in a decolored state.
The reversibly thermochromic composition comprises three ingredients, i.e., (a) an electron-donating compound, (b) an electron-accepting compound, and (c) a reaction medium determining the temperatures at which the color reactions between components (a) and (b) take place. As this composition can be used, for example, the compositions proposed by the applicant which are disclosed in U.S. Pat. Nos. 4,028,118 and No. 4,732,810.
This composition changes in color at a given temperature (color change point) in such a manner that the composition is in a decolored state at temperatures not lower than the color change point and is in a colored state at temperatures lower than the color change point. At ordinary temperature, the composition exists only in specific one of the two states. Namely, the other state is maintained only during the period in which heat or cold required for the development of this state is kept being applied, and the composition returns to the original ordinary-temperature state upon removal of the heat or cold. This composition is a reversibly thermochromic composition of the heating decoloration type which shows such a thermochromic behavior in which the hysteresis range is relatively narrow.
Also usable is the thermochromic composition which is disclosed in U.S. Pat. No. 4,720,301. This composition shows enhanced hysteresis. Namely, plotting the color density against temperature gives a curve showing that the composition changes in color along routes which differ considerably between the case where the composition is heated from a temperature on the lower-temperature side of the color change temperature range and in the reverse case where the composition is cooled from a temperature on the higher-temperature side of the color change temperature range. This composition is a thermochromic color-memorizing composition of the heating decoloration type in which the colored state in the range of temperatures not higher than the lower color change point and the decolored state in the range of temperatures not lower than the higher color change point can be alternately memorized and retained even after the heat or cold required for the color change has been removed.
Furthermore, a reversibly thermochromic composition of the heating coloration type can also be used which contains as an electron-accepting compound (b) a specific alkoxyphenol compound having a linear or branched alkyl group having 3 to 18 carbon atoms.
The reversibly thermochromic composition is microencapsulated and used as a microencapsulated pigment. This microencapsulation enables the composition to develop a bright color having a high density and satisfy practical properties such as homogeneity, dispersion stability, chemical resistance, and heat resistance.
For the microencapsulation, known techniques can be used. Examples thereof include interfacial polymerization, in-situ polymerization, in-liquid curing coating, phase separation from an aqueous solution, phase separation from an organic solvent, melt dispersion cooling, air-suspension coating, and spray drying.
Before the microencapsulated pigment is subjected to practical use, the surface properties of the microcapsules may be modified according to purposes.
The microencapsulated pigment is dispersed into a medium containing the resin to prepare a coloring material such as an ink or coating composition. This coloring material is applied to a substrate to thereby form a reversibly thermochromic layer.
Adding a non-thermochromic dye or pigment enables a color change from a colored opaque state (1) to a colored transparent state (2).
For forming the thermochromic layer, known techniques can be used. Examples thereof include printing techniques such as screen printing, offset printing, gravure printing, coater printing, tampon printing, and transfer printing and coating techniques such as brush coating, spray coating, electrostatic coating, electrodeposition, curtain coating, roller coating, and dip coating.
Examples of the material of the substrate include papers, synthetic papers, artificial leathers, natural leathers, plastics, glasses, porcelains and pottery, woods, stones, and metals.
The substrate may have a flat shape or may have recesses and protrusions.
Since the reversibly thermochromic layer of the laminate member of the invention undergoes alternate color changes between a colorless transparent state and a colored opaque state with temperature, the condition on the opposite side of the substrate can be perceived/hidden when the substrate is made of a transparent material. This laminate member can be applied, for example, to a reversibly thermochromic three-dimensional object comprising a three-dimensional substrate made of a transparent resin, the reversibly thermochromic layer formed on the substrate, and an appropriate shaped article enclosed in the three-dimensional substrate. In this reversibly thermochromic object, the shaped article placed inside can be perceived when the thermochromic layer is in a transparent state, and can be hidden when the thermochromic layer is in a colored opaque state.
Examples of the shaped article include dolls and toys modeled on, e.g., animals, vehicles, buildings, plants, foods, or stones.
The shaped article enclosed in the three-dimensional object is preferably in close contact with the three-dimensional object. Namely, the reversibly thermochromic three-dimensional object preferably has such a constitution that it has no space at the interface between the outer surface of the shaped article and the three-dimensional object. This is because the absence of spaces enables the shaped article to be clearly perceived.
The metallic glossy layer which may be formed on the reversibly thermochromic layer will be explained next.
The metallic glossy layer is a layer comprising a binder resin and, fixedly dispersed therein, a metallic luster pigment based on a transparent material, as a core material, selected from natural micas, synthetic micas, flat pieces of glasses, and flaky aluminum oxide.
The metallic glossy layer not only imparts any of various colors with a metallic luster to the reversibly thermochromic layer, but also functions as a light-shielding layer. Namely, due to its light-absorbing (or light-reflecting) function and light-shielding function, the metallic glossy layer absorbs or reflects at least part of ultraviolet and visible rays, which may adversely influence the functions of the reversibly thermochromic layer. Thus, the metallic glossy layer further has the effect of improving the light resistance of the reversibly thermochromic layer.
Effective metallic luster pigments based on a natural mica as a core material include one obtained by coating the surface of natural-mica particles with titanium oxide, one obtained by coating the surface of natural-mica particles with titanium oxide and then further coating the coated particles with iron oxide, and one obtained by coating the surface of natural-mica particles with titanium oxide and then further coating the coated particles with a non-thermochromic dye or pigment (preferably in an amount of from 0.5 to 10% by weight). Specific examples thereof include: a gold metallic luster pigment having a particle size of from 5 to 50 xcexcm obtained by coating the surface of a natural mica with 41 to 44% by weight titanium-oxide; a gold metallic luster pigment having a particle size of from 5 to 60 xcexcm obtained by coating the surface of a natural mica with 30 to 38% by weight titanium oxide and further coating the coated particles with 0.5 to 10% by weight non-thermochromic color pigment; a silver metallic luster pigment having a particle size of from 5 to 100 xcexcm obtained by coating the surface of a natural mica with 16 to 39% by weight titanium oxide; a metallic luster pigment obtained by coating the surface of a natural mica with 45 to 58% by weight titanium oxide; and a metallic luster pigment obtained by coating the surface of a natural mica with 45 to 58% by weight titanium oxide and then further coating the coated particles with 0.5 to 10% by weight non-thermochromic color dye or pigment. The xe2x80x9c% by weightxe2x80x9d used above is based on the total weight of the metallic luster pigment.
Metallic luster pigments based on a synthetic mica as a core material have a lower impurity content and a lower content of iron and other metal ions, which are a coloring factor, as compared with the metallic luster pigments based on a natural mica. Because of this, the pigments based on a synthetic mica have excellent transparency and is highly lustrous and glittering. Effective examples thereof include a pigment which is obtained by coating the surface of a synthetic mica with one or more metal oxides comprising titanium oxide as the main component and has an average particle thickness of from 0.1 to 5 xcexcm and an average particle diameter of from 2 to 1,000 xcexcm. This pigment has a metallic luster of a gold, silver, or another color depending on the degree of coating with the metal oxides. It is so transparent that the color tone of the underlying reversibly thermochromic layer can be clearly perceived.
Examples of the synthetic mica include ones represented by the following formula. One example is KMg3(AlSi3O10)F2.
xe2x80x83X1/3xe2x88x921Y2xe2x88x923Z4O10F2xe2x80x83xe2x80x83(1)
(In formula (1), X represents Na+, Li+, K+, Ca2+, Sr2+, or Ba2+; Y represents one or more members selected from Mg2+, Li+, Ni2+, Co2+, Zn2+, Mn2+, Al3+, Cr3+, and Ti3+; and Z represents one or more members selected from Al3+, Si4+, GE4+, and B3+.)
The shape of the mica is not particularly limited, and examples thereof include flat shapes and flaky shapes.
Examples of the metal oxides with which the surface of the synthetic mica is coated include oxides of metals such as titanium, zirconium, chromium, vanadium, and iron. However, it is preferred to use one or more metal oxides comprising titanium oxide as the main component.
The metallic luster pigments based on a synthetic mica as a core material are effective when the average particle thickness thereof is generally from 0.1 to 5 xcexcm and the average particle diameter thereof is generally from 2 to 1,000 xcexcm, preferably from 2 to 500 xcexcm, more preferably from 2 to 200 xcexcm. This average particle diameter means the average particle diameter which is determined by laser diffractometry and is the particle diameter corresponding to the 50% point in a cumulative median diameter distribution on a volume basis.
Specific examples of the metallic luster pigments comprising a synthetic mica whose surface is coated with a metal oxide include xe2x80x9cUltimicaxe2x80x9d (trade name) SB-100 (5-30 xcexcm; silver), SD-100 (10-60 xcexcm; silver), SE-100 (15-100 xcexcm; silver), SF-100 (44-150 xcexc; silver), SH-100 (150-600 xcexcm; silver), YB-100 (5-30 xcexcm; gold), YD-100 (10-60 xcexcm; gold), YE-100 (15-100 xcexcm; gold), YF-100 (44-150 xcexcm; gold), RB-100 (5-300 xcexcm; metallic red), RD-100 (10-60 xcexcm; metallic red), RE-100 (15-100 xcexcm; metallic red), RF-100 (44-150 xcexcm; metallic red), RBB-100 (5-30 xcexcm; metallic purple), RBD-100 (10-60 xcexcm; metallic purple), RBE-100 (15-100 xcexcm; metallic purple), RBF-100 (44-150 xcexcm; metallic purple), VB-100 (5-30 xcexcm; metallic violet), VD-100 (10-60 xcexcm; metallic violet), VE-100 (15-100 xcexcm; metallic violet), VF-100 (44-150 xcexcm; metallic violet), BB-100 (5-30 xcexcm; metallic blue), BD-100 (10-60 xcexcm; metallic blue), BE-100 (15-100 xcexcm; metallic blue), BF-100 (44-150 xcexcm; metallic blue), GB-100 (5-30 xcexcm; metallic green), GD-100 (10-60 xcexcm; metallic green), GE-100 (15-100 xcexcm; metallic green), and GF-100 (44-150 xcexcm; metallic green), all manufactured by Nihon Kokenkogyo K.K.
Examples of the metallic luster pigments obtained by coating the surface of flat glass pieces as a core material with titanium oxide include such metallic luster pigments which have a gold, silver, or another metallic color depending on the degree of coating with titanium oxide. Specific examples thereof include the pigments obtained by coating glass flakes with titanium oxide which are manufactured by Nippon Sheet Glass Co., Ltd. and sold under the trade name of xe2x80x9cMetashinexe2x80x9d RCFSX-5450TS(6041) (average thickness, 5xc2x12 xcexcm; average particle size, 450xc2x1145 xcexcm; gold), RCFSX-5200TS(6042) (average thickness, 5xc2x12 xcexcm; average particle size, 200xc2x170 xcexcm; silver), RCFSX-5140TS(6043) (average thickness, 5xc2x12 xcexcm; average particle size, 140xc2x145 xcexcm; silver), RCFSX-5080TS(6044) (average thickness, 5xc2x12 xcexcm; average particle size, 80xc2x130 xcexcm; silver), RCFSX-2080TS(6046) (average thickness, 2xc2x11 xcexcm; average particle size, 80xc2x130 xcexcm; silver), RCFSX-K120TS(6043) (average thickness, 20xc2x15 xcexcm; average particle size, 120xc2x120 xcexcm; silver), RCFSX-5090RC(8052) (average thickness, 5xc2x12 xcexcm; average particle size, 90xc2x130 xcexcm; gold), RCFSX-5090RC(8053) (average thickness, 5xc2x12 xcexcm; average particle size, 90xc2x130 xcexcm; metallic green), RCFSX-5090RC(8069) (average thickness, 5xc2x12 xcexcm; average particle size, 90xc2x130 xcexcm; metallic blue), RCFSX-5090RC(8070) (average thickness, 5xc2x12 xcexcm; average particle size, 90xc2x130 xcexcm; metallic purple), RCFSX-5090RC(8071) (average thickness, 5xc2x12 xcexcm; average particle size, 90xc2x130 xcexcm; metallic red), RCFSX-1040RC(9543) (average thickness, 1 xcexcm; average particle size, 40 xcexcm; silver), RCFSX-1040RC(9544) (average thickness, 1 xcexcm; average particle size, 40 xcexcm; gold), RCFSX-1040RC(9546) (average thickness, 1 xcexcm; average particle size, 40 xcexcm; metallic red), RCFSX-1040RC(9548) (average thickness, 1 xcexcm; average particle size, 40 xcexcm; metallic blue), RCFSX-1040RC(9549) (average thickness, 1 xcexcm; average particle size, 40 xcexcm; metallic green), RCFSX-1020RC(9550) (average thickness, 1 xcexcm; average particle size, 20 xcexcm; silver), RCFSX-1020RC(9551) (average thickness, 1 xcexcm; average particle size, 20 xcexcm, gold), RCFSX-1020RC(9553) (average thickness, 1 xcexcm; average particle size, 20 xcexcm; metallic red), and RCFSX-1020RC(9555) (average thickness, 1 xcexcm; average particle size, 20 xcexcm; metallic blue).
The metallic luster pigments obtained by coating the surface of flaky aluminum oxide as a core material with a metal oxide will be explained below.
Because the core material is flaky aluminum oxide, this kind of metallic luster pigment has a lower impurity content and is more lustrous than the pigments based on a natural mica.
Examples of the metal oxide with which the surface of the aluminum oxide is coated include oxides of metals such as titanium, zirconium, chromium, vanadium, and iron. However, it is preferred to use one or more metal oxides comprising titanium oxide as the main component. Examples of the metallic luster pigments include ones which have a gold, silver, or another metallic color depending on the degree of coating with the metal oxide.
These metallic luster pigments preferably have an average thickness of from 0.1 to 5 xcexcm and an average particle diameter of from 2 to 200 xcexcm.
By using a metallic luster pigment having a thickness and average particle diameter within the respective ranges shown above, it is possible to obtain a metallic glossy image which is evenly lustrous and a thermochromic image undergoing distinct color changes. This average particle diameter means the average particle diameter which is determined by laser diffractometry and is the particle diameter corresponding to the 50% point in a cumulative median diameter distribution on a volume basis.
Specific examples of the metallic luster pigments obtained by coating the surface of flaky aluminum oxide with a metal oxide include the pigment manufactured by Merck and Co., Inc. and sold under the trade name of xe2x80x9cXirallicxe2x80x9d T50-10 (10-30 xcexcm; silver).
The metallic luster pigments obtained by coating a core material selected from natural micas, synthetic micas, flat pieces of glasses, and flaky aluminum oxide with a metal oxide have transparency as well as a metallic luster. Of these metallic luster pigments, those obtained by coating a core material selected from synthetic micas, flat pieces of glasses, and flaky aluminum oxide with a metal oxide are suitable for use in the invention because they are superior in transparency.
The metallic glossy layer in the invention has a light transmittance of preferably 5% or higher, more preferably 10% or higher.
Such a light transmittance produces the following effect. When the reversibly thermochromic layer is in a colored state, the metallic glossy layer shows light-shielding properties and a metallic lustrous color is perceived. When the reversibly thermochromic layer is in a decolored state, no metallic lustrous color is perceived and the metallic glossy layer shows excellent transparency.
In the case where the substrate has transparency, an article placed inside or on the back side of the laminate member can be clearly perceived through the laminate member when the light transmittance of the laminate member itself is 5% or higher at the time when the reversibly thermochromic layer is in a decolored state.
In producing the reversibly thermochromic light-shielding/light-transmitting laminate member of the invention, a reversibly thermochromic ink is suitably applied to a substrate. The ink comprises a reversibly thermochromic microencapsulated pigment containing a reversibly thermochromic composition comprising (a) an electron-donating color-forming organic compound, (b) an electron-accepting compound, and (c) a reaction medium determining the temperatures at which the color reactions of component (a) with component (b) take place and a vehicle containing a transparent resin having a tensile elongation at break of 350% or lower. The resultant coating is dried to form a reversibly thermochromic layer, whereby the laminate member of the invention is obtained.
In the case where a metallic glossy layer is to be formed on the reversibly thermochromic layer, a metallic luster ink comprising a vehicle containing a metallic luster pigment is applied to the thermochromic layer to form the metallic glossy layer.