The present invention relates to a polyimide film having highly improved mechanical properties and a production process thereof.
A wholly aromatic polyimide has been widely used in industry due to its excellent heat resistance and mechanical properties. Particularly, its film occupies an important position as a substrate for a thin-layer electronic part including an electronic packaging application. In recent years, a thinner polyimide film is desired in response to a strong demand for smaller electronic parts. However, it is an essential requirement from viewpoints of actual use and handling of the film that the film have high rigidity along with a decrease in thickness. Although the wholly aromatic polyimide film has a rigid structure, it cannot be necessarily said that the film has a truly high Young""s modulus as compared with, for example, a wholly aromatic polyamide film. It is a current situation that a Young""s modulus of a commercially available polyimide film having the highest Young""s modulus is merely as high as 9 GPa.
As a method of achieving a high Young""s modulus in the wholly aromatic polyimide film, (1) application of a chemical structure which is rigid and has high linearity to a molecular skeleton constituting a polyimide and (2) orientation of molecules of the polyimide by a physical technique are considered. As the chemical structure of (1), a raw material to attain the chemical structure has been studied by use of various combinations of pyromellitic acid or 3,3xe2x80x2,4,4xe2x80x2-biphenyltetracarboxylic acid as an acid component and paraphenylenediamine, benzidine or nucleus substituted compounds thereof as an amine component. Of the studied raw materials, polyparaphenylenepyromellitimide is the most promising raw material as a raw material for a film having a high Young""s modulus since it has the highest theoretical elastic modulus (refer to Tashiro et al., Journal of Society of Textiles, Vol. 43, p. 78 (1987)) and its raw materials are inexpensive. However, despite its potential, a conventional polyparaphenylenepyromellitimide film is extremely brittle, and a polyparaphenylenepyromellitimide film which is balanced and has a high Young""s modulus is not yet attained.
As a method for overcoming the situation, a method of chemically cyclizing a polyamide acid solution obtained by a reaction between paraphenylenediamine and pyromellitic anhydride is proposed in JP-A 1-282219. However, a Young""s modulus of a polyparaphenylenepyromellitimide film obtained by the method is merely as high as 8.5 GPa.
JP-A 6-172529 discloses that a film having a Young""s modulus of 20.1 GPa is obtained by flow-casting a dope produced by adding a large amount of acetic anhydride to a polyamide acid solution obtained by a reaction between nucleus-substituted paraphenylenediamine and pyromellitic anhydride, drying the cast dope at low temperatures under a reduced pressure and heat-treating the resulting dope. However, this method is an industrially unrealistic technique since it requires dry treatment at low temperatures over a few hours. Further, it is also disclosed that a film which can be obtained when the technique is applied to polyparaphenylenepyromellitimide is only a film which is so brittle that it cannot undergo even mechanical measurements. Therefore, the effect of the technique is limited. Thus, a technique for attaining a film having a high Young""s modulus which can be widely used in aromatic polyimides which are rigid is not completed. In particular, a polyparaphenylenepyromellitimide film having a high Young""s modulus and practical toughness is not known.
Meanwhile, as a method for orienting a polyimide by stretching, a method in which a polyamic acid solution which is a precursor of polyparaphenylenepyromellitimide is formed into a film, dried, monoaxially stretched in a solvent and formed into an imide is disclosed in Polymer Articles, Vol. 56, No. 5, pp. 282 to 290. Further, a method in which a precursor polyamic ester having an ester group of a long chain (having 10 to 18 carbon atoms) introduced into a polymer chain is wet-spun, oriented by stretching and formed into an imide by heating is proposed in Polymer Preprint Japan, Vol. 41, No. 9 (1992) 3752. However, both of the publications set forth nothing about a biaxially stretched film which is balanced in a plane.
Therefore, a polyparaphenylenepyromellitimide film with a high Young""s modulus which is balanced in a plane is not yet known.
An object of the present invention is to provide a polyimide film having mechanical properties, particularly a Young""s modulus, improved by a high degree of orientation which could not be achieved by the prior art.
Another object of the present invention is to provide a polyparaphenylenepyromellitimide film having a high Young""s modulus.
Another object of the present invention is to provide a process for producing the above film of the present invention.
Other objects and advantages of the present invention will be apparent from the following description.
According to the present invention, firstly, the above objects and advantages of the present invention are achieved by a polyimide film which comprises a polyimide consisting essentially of a diamine component and a tetracarboxylic acid component, the diamine component comprising a p-phenylenediamine component whose amount is more than 80 mol % to 100 mol % and an aromatic diamine component other than p-phenylenediamine whose amount is 0 mol % to less than 20 mol % and the tetracarboxylic acid component comprising pyromellitic acid whose amount is more than 80 mol % and an aromatic tetracarboxylic acid component other than pyromellitic acid whose amount is 0 mol % to less than 20 mol %, and which has two directions each having a Young""s modulus of higher than 10 GPa and perpendicular to each other in a film plane.
According to the present invention, secondly, the above objects and advantages of the present invention are achieved by a process (hereinafter may be referred to as xe2x80x9cfirst production processxe2x80x9d) for producing a polyimide film which comprises the steps of:
(1) preparing a solution of polyamic acid in a solvent, the polyamic acid consisting essentially of a diamine component and a tetracarboxylic acid component, the diamine component comprising a p-phenylenediamine component whose amount is more than 80 mol % to 100 mol % and an aromatic diamine component other than p-phenylenediamine whose amount is 0 mol % to less than 20 mol % and the tetracarboxylic acid component comprising pyromellitic acid whose amount is more than 80 mol % and an aromatic tetracarboxylic acid component other than pyromellitic acid whose amount is 0 mol % to less than 20 mol %, the solvent comprising at least one solvent selected from the group consisting of N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and 1,3-dimethylimidazolidinone,
(2) immersing a film obtained by flow casting the solution prepared in the above (1) on a substrate into an isoimidating solution produced by dissolving dicyclohexylcarbodiimide in at least one solvent selected from the above solvents, with the film being attached to the substrate, so as to form a gelled film in which at least a portion of the polyamic acid has been converted into a polyisoimide,
(3) separating the obtained gelled film from the substrate, rinsing the film as required, and then biaxially stretching the film, and
(4) subjecting the resulting film to heat treatment, as required, after rinsing the obtained biaxially stretched film to remove the solvent therefrom, so as to form a biaxially oriented polyimide film.
Further, according to the present invention, thirdly, the above objects and advantages of the present invention are achieved by a process (hereinafter may be referred to as xe2x80x9csecond production processxe2x80x9d) for producing a polyimide film which comprises the steps of:
(1) preparing a solution of polyamic acid in a solvent, the polyamic acid consisting of a diamine component and a tetracarboxylic acid component, the diamine component comprising a p-phenylenediamine component whose amount is more than 80 mol % to 100 mol % and an aromatic diamine component other than p-phenylenediamine whose amount is 0 mol % to less than 20 mol % and the tetracarboxylic acid component comprising pyromellitic acid whose amount is more than 80 mol % and an aromatic tetracarboxylic acid component other than pyromellitic acid whose amount is 0 mol % to less than 20 mol %, the solvent comprising at least one solvent selected from the group consisting of N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and 1,3-dimethylimidazolidinone,
(2) immersing a film obtained by flow casting the solution prepared in the above (1) on a substrate into a mixture comprising at least one solvent selected from the above solvents, acetic anhydride and an organic amine compound, with the film being attached to the substrate, so as to form a gelled film in which at least a portion of the polyamic acid has been converted into a polyimide or polyisoimide,
(3) separating the obtained gelled film from the substrate, rinsing the film as required, and then biaxially stretching the film, and
(4) subjecting the resulting film to heat treatment, as required, after rinsing the obtained biaxially stretched film to remove the solvent therefrom, so as to form a biaxially oriented polyimide film.
Firstly, the polyimide film of the present invention will be described. The diamine component constituting the polyimide comprises p-phenylenediamine and an aromatic diamine other than p-phenylenediamine.
Illustrative examples of the aromatic diamine component other than p-phenylenediamine include m-phenylenediamine, 1,4-diaminonaphthalene, 1,5-diaminonaphthalene, 1,8-diaminonaphthalene, 2,6-diaminonaphthalene, 2,7-diaminonaphthalene, 2,6-diaminoanthracene, 2,7-diaminoanthracene, 1,8-diaminoanthracene, 2,4-diaminotoluene, 2,5-diamino(m-xylene), 2,5-diaminopyridine, 2,6-diaminopyridine, 3,5-diaminopyridine, 2,4-diaminotoluenebenzidine, 3,3xe2x80x2-diaminobiphenyl, 3,3xe2x80x2-dichlorobenzidine, 3,3xe2x80x2-dimethylbenzidine, 3,3xe2x80x2-dimethoxybenzidine, 2,2xe2x80x2-diaminobenzophenone, 4,4xe2x80x2-diaminobenzophenone, 3,3xe2x80x2-diaminodiphenyl ether, 4,4xe2x80x2-diaminodiphenyl ether, 3,4xe2x80x2-diaminodiphenyl ether, 3,3xe2x80x2-diaminodiphenylmethane, 4,4xe2x80x2-diaminodiphenylmethane, 4,4xe2x80x2-diaminodiphenylmethane, 3,4xe2x80x2-diaminodiphenylsulfone, 4,4xe2x80x2-diaminodiphenylsulfone, 3,3xe2x80x2-diaminodiphenylsulfide, 3,4xe2x80x2-diaminodiphenylsulfide, 4,4xe2x80x2-diaminodiphenylsulfide, 4,4xe2x80x2-diaminodiphenyl thioether, 4,4xe2x80x2-diamino-3,3xe2x80x2,5,5xe2x80x2-tetramethyldiphenyl ether, 4,4xe2x80x2-diamino-3,3xe2x80x2,5,5xe2x80x2-tetraethyldiphenyl ether, 4,4xe2x80x2-diamino-3,3xe2x80x2,5,5xe2x80x2-tetramethyldiphenylmethane, 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 2,6-bis(3-aminophenoxy)pyridine, 1,4-bis(3-aminophenylsulfonyl)benzene, 1,4-bis(4-aminophenylsulfonyl)benzene, 1,4-bis(3-aminophenyl thioether)benzene, 1,4-bis(4-aminophenyl thioether)benzene, 4,4xe2x80x2-bis(3-aminophenoxy)diphenyl sulfone, 4,4xe2x80x2-bis(4-aminophenoxy)diphenyl sulfone, bis(4-aminophenyl)amine, bis(4-aminophenyl)-N-methylamine, bis(4-aminophenyl)-N-phenylamine, bis(4-aminophenyl)phosphine oxide, 1,1-bis(3-aminophenyl)ethane, 1,1-bis(4-aminophenyl)ethane, 2,2-bis(3-aminophenyl)propane, 2,2-bis(4-aminophenyl)propane, 2,2-bis(4-amino-3,5-dimethylphenyl)propane, 4,4xe2x80x2-bis(4-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]ether, bis[4-(4-aminophenoxy)phenyl]methane, bis[3-methyl-4-(4-aminophenoxy)phenyl]methane, bis[3-chloro-4-(4-aminophenoxy)phenyl]methane, bis[3,5-dimethyl-4-(4-aminophenoxy)phenyl]methane, 1,1-bis[4-(4-aminophenoxy)phenyl]ethane, 1,1-bis[3-methyl-4-(4-aminophenoxy)phenyl]ethane, 1,1-bis[3-chloro-4-(4-aminophenoxy)phenyl]ethane, 1,1-bis[3,5-dimethyl-4-(4-aminophenoxy)phenyl]ethane, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[3-methyl-4-(4-aminophenoxy)phenyl]propane, 2,2-bis[3-chloro-4-(4-aminophenoxy)phenyl]propane, 2,2-bis[3,5-dimethyl-4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis[3-methyl-4-(4-aminophenoxy)phenyl]butane, 2,2-bis[3,5-dimethyl-4-(4-aminophenoxy)phenyl]butane, 2,2-bis[3,5-dibromo-4-(4-aminophenoxy)phenyl]butane, 1,1,1,3,3,3-hexafluoro-2,2-bis(4-aminophenyl)propane, 1,1,1,3,3,3-hexafluoro-2,2-bis[3-methyl-4-(4-aminophenoxy) phenyl]propane, and substitution products thereof resulting from substitution of a halogen atom or alkyl group into an aromatic nucleus.
The diamine component comprises either p-phenylenediamine alone or a combination of p-phenylenediamine and an aromatic diamine other than p-phenylenediamine which is exemplified by the compounds enumerated above. In the latter case, p-phenylenediamine constitutes more than 80 mol %, preferably more than 90 mol %, of a total amount of the diamine component, that is, an aromatic diamine other than p-phenylenediamine constitutes less than 20 mol %, preferably less than 10 mol %, of the total amount of the diamine component.
Meanwhile, the tetracarboxylic acid component constituting the polyimide comprises pyromellitic acid and an aromatic tetracarboxylic acid other than pyromellitic acid.
Illustrative examples of the aromatic tetracarboxylic acid component other than pyromellitic acid include 1,2,3,4-benzenetetracarboxylic dianhydride, 2,3,5,6-pyridinetetracarboxylic dianhydride, 2,3,4,5-thiophenetetracarboxylic dianhydride, 2,2xe2x80x2,3,3xe2x80x2-benzophenonetetracarboxylic dianhydride, 2,3xe2x80x2,3,4xe2x80x2-benzophenonetetracarboxylic dianhydride, 3,3xe2x80x2,4,4xe2x80x2-benzophenonetetracarboxylic dianhydride, 3,3xe2x80x2,4,4xe2x80x2-biphenyltetracarboxylic dianhydride, 2,2xe2x80x2,3,3xe2x80x2-biphenyltetracarboxylic dianhydride, 2,3,3xe2x80x2,4xe2x80x2-biphenyltetracarboxylic dianhydride, 3,3xe2x80x2,4,4xe2x80x2-p-terphenyltetracarboxylic dianhydride, 2,2xe2x80x2,3,3xe2x80x2-p-terphenyltetracarboxylic dianhydride, 2,3,3xe2x80x2,4xe2x80x2-p-terphenyltetracarboxylic dianhydride, 1,2,4,5-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, 1,2,5,6-anthracenetetracarboxylic dianhydride, 1,2,6,7-phenanthrenetetracarboxylic dianhydride, 1,2,7,8-phenanthrenetetracarboxylic dianhydride, 1,2,9,10-phenanthrenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,6-dichloronaphthalene-1,4,5,8-tetracarboxylic dianhydride, 2,7-dichloronaphthalene-1,4,5,8-tetracarboxylic dianhydride, 2,3,6,7-tetrachloronaphthalene-1,4,5,8-tetracarboxylic dianhydride, 1,4,5,8-tetrachloronaphthalene-2,3,6,7-tetracarboxylic dianhydride, bis(2,3-dicarboxyphenyl)ether dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, bis(2,3-dicarboxyphenyl)sulfone dianhydride, bis(3,4-dicarboxyphenyl)sulfone dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, 1,1-bis(3,4-dicarboxyphenyl)ethane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, 2,6-bis(3,4-dicarboxyphenyl)pyridine dianhydride, 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-dicarboxyphenyl) propane dianhydride, and bis(3,4-dicarboxyphenyl)dimethylsilane dianhydride.
The tetracarboxylic acid component comprises either pyromellitic acid alone or a combination of pyromellitic acid and an aromatic tetracarboxylic acid other than pyromellitic acid which is exemplified by the compounds enumerated above. In the latter case, pyromellitic acid constitutes more than 80 mol %, preferably more than 90 mol %, of a total amount of the tetracarboxylic acid component, that is, an aromatic tetracarboxylic acid other than pyromellitic acid constitutes less than 20 mol %, preferably less than 10 mol %, of the total amount of the tetracarboxylic acid component.
A film of the present invention which comprises a polyimide composed of a diamine component comprising 100 mol % of the p-phenylenediamine component and 100 mol % of the pyromellitic acid component exhibits a more desirable Young""s modulus.
The polyimide constituting the polyimide film of the present invention preferably has a percentage of imido groups of not lower than 95%. When the percentage of imido groups is lower than 95%, hydrolysis resistance of the polyimide film deteriorates. The percentage of imido groups is defined in Examples.
The polyimide film of the present invention has a high Young""s modulus which has heretofore not been attained and a practically excellent characteristic that a balance of Young""s moduli in a film plane is excellent. That is, two directions each having a Young""s modulus of higher than 10 GPa and perpendicular to each other are present in the film plane. Preferably, two directions each having a Young""s modulus of higher than 12 GPa and perpendicular to each other are present in the film plane.
The present inventors have found that brittleness of the conventionally known polyparaphenylenepyromellitimide having such a high Young""s modulus can be overcome by imparting a special fine structure to the polyimide film. That is, in the case of the polyimide film of the present invention, the following relational expressions (1), (2) and (3) preferably hold between a refractive index nz in a direction perpendicular to the film plane and a density d of the film.
1.61 greater than nz greater than 1.55xe2x80x83xe2x80x83(1)
1.57 greater than d greater than 1.46xe2x80x83xe2x80x83(2)
2.0dxe2x88x921.33 greater than nz greater than 1.5dxe2x88x920.77xe2x80x83xe2x80x83(3)
nz is a measure for orientation of molecules of the polyimide. A decrease in value of nz indicates an increase in degree of orientation in the plane. When nz is 1.61 or larger, a low Young""s modulus is exhibited due to insufficient orientation, while when nz is 1.55 or smaller, stretchability of the film becomes low due to excessive orientation. The density d is a measure associated with crystallinity of the polyimide and a degree of compactness of the fine structure thereof. When d is larger than 1.57, toughness of the film is insufficient, while when it is smaller than 1.46, the film has insufficient crystallinity, an increased water absorption property and poor dimensional stability. It is known that in the case of a general polymer, a high density can be attained by increasing a degree of orientation. In the case of the polyimide film of the present invention, surprisingly, when nz is decreased and the density d is lowered by orientation, a polyimide film having both high strength and a high Young""s modulus can be attained. When nz is larger than 2.0d-1.33, orientation is insufficient in contrast to crystallinity, so that the film becomes brittle, while when nz is smaller than 1.5d-0.77, the crystallinity is insufficient in contrast to the orientation, so that the film has an increased water absorption property and poor dimensional stability.
In this case, when d is larger than 1.57, toughness of the film is insufficient, while when it is smaller than 1.46, the film has insufficient crystallinity, an increased water absorption property and poor dimensional stability.
The polyimide film of the present invention preferably has a tensile strength in one direction of not lower than 0.3 GPa, more preferably not lower than 0.4 GPa.
The present inventors have studied a technique for stretching an aromatic polyimide having a rigid structure to a high degree so as to orient molecules thereof. As a result, they have found it based on a fact that a gel prepared by chemically treating a precursor amic acid by a specific method exhibits high stretchability at low temperatures near room temperature, that a polyimide film having a significantly improved Young""s modulus and balanced mechanical properties in a plane can be obtained by stretching the gel in a swollen state and then heat treating the stretched film. Further, they have also found that when the gel preparation method and the gel stretching method are applied to polyparaphenylenepyromellitimide, polyparaphenylenepyromellitimide with a balanced Young""s modulus and practical strength and toughness which has heretofore been unable to be attained can be obtained. The present invention has been completed by these findings.
Next, the processes of the present invention for producing a polyimide film will be described in detail.
The first production process of the present invention comprises the following steps (1) to (4), that is,
(1) preparing a solution of polyamic acid in a solvent, the polyamic acid consisting of a diamine component and a tetracarboxylic acid component, the diamine component comprising p-phenylenediamine whose amount is more than 80 mol % to 100 mol % and an aromatic diamine component other than p-phenylenediamine whose amount is 0 mol % to less than 20 mol % and the tetracarboxylic acid component comprising pyromellitic acid whose amount is more than 80 mol % and an aromatic tetracarboxylic acid component other than pyromellitic acid whose amount is 0 mol % to less than 20 mol %, the solvent comprising at least one solvent selected from the group consisting of N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and 1,3-dimethylimidazolidinone,
(2) immersing a film obtained by flow casting the solution prepared in the above (1) on a substrate into an isoimidating solution produced by dissolving dicyclohexylcarbodiimide in at least one solvent selected from the above solvents, with the film being attached to the substrate, so as to form a gelled film in which at least a portion of the polyamic acid has been converted into a polyisoimide,
(3) separating the obtained gelled film from the substrate, rinsing the film as required, and then biaxially stretching the film, and
(4) subjecting the resulting film to heat treatment, as required, after rinsing the obtained biaxially stretched film to remove the solvent therefrom, so as to form a biaxially oriented polyimide film.
In the step (1), a solution of polyamic acid in a solvent is prepared. The polyamic acid comprises such a diamine component and tetracarboxylic acid component as described above. Specific examples of an aromatic diamine other than p-phenylenediamine which constitutes the diamine component and an aromatic tetracarboxylic acid other than pyromellitic acid are the same as those enumerated for the polyimide. The diamine component of the polyamic acid comprises either p-phenylenediamine alone or a combination of p-phenylenediamine and such an aromatic diamine other than p-phenylenediamine as those enumerated above. In the latter case, p-phenylenediamine constitutes more than 80 mol %, preferably more than 90 mol %, of a total amount of the diamine component, that is, the aromatic diamine other than p-phenylenediamine constitutes less than 20 mol %, preferably less than 10 mol %, of the total amount of the diamine component.
Meanwhile, the tetracarboxylic acid component of the polyamic acid comprises either pyromellitic acid alone or a combination of pyromellitic acid and such an aromatic tetracarboxylic acid other than pyromellitic acid as those enumerated above. In the latter case, pyromellitic acid constitutes more than 80 mol %, preferably more than 90 mol %, of a total amount of the tetracarboxylic acid component, that is, the aromatic tetracarboxylic acid other than pyromellitic acid constitutes less than 20 mol %, preferably less than 10 mol %, of the total amount of the tetracarboxylic acid component.
Further, in producing the polyamic acid, these diamine and acid anhydride are desirably used in a diamine to acid anhydride molar ratio of preferably 0.90 to 1.10, more preferably 0.95 to 1.05.
Terminals of the polyamic acid are preferably blocked. The terminals of the polyamic acid may be blocked by use of a terminal blocking agent. Illustrative examples of the terminal blocking agent include phthalic anhydride and substitution products thereof, hexahydrophthalic anhydride and substitution products thereof, and succinic anhydride and substitution products thereof, and its amine component is exemplified by aniline and substitution products thereof. An amine component is exemplified by aniline and substitution products thereof.
As the solvent, N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and 1,3-dimethylimidazolidinone are used. These solvents can be used solely or in combination of two or more.
According to the step (1), a solution of polyamic acid in a solvent which has a solid content of preferably 0.5 to 30 wt %, more preferably 2 to 15 wt %, is prepared.
Then, in the step (2), a film obtained by flow casting the solution prepared in the above step (1) on a substrate is immersed in an isoimidated solution together with the substrate.
To flow-cast the solution obtained in the above step (1) on the substrate, any film forming method such as generally known wet and dry molding methods may be used. The film forming method is exemplified by a die extrusion method, casting using an applicator and a method using a coater. As the substrate on which the polyamic acid is flow-cast, a metal belt, a metal casting drum or the like can be used. Alternatively, the solution of the polyamic acid may be flow-cast onto a film of an organic polymer such as a polyester or polypropylene and then introduced into a condensation agent solution directly. These steps are preferably carried out under a low-moisture atmosphere. The isoimidated solution is prepared by dissolving dicyclohexylcarbodiimide in at least one solvent selected from the same solvents as used in the above step (1).
The concentration of hexylcarbodiimide in the isoimidated solution is not particularly limited but is preferably 0.5 to 99 wt % to cause a reaction to fully proceed. A reaction temperature is not particularly limited but may be a temperature within a range from a freezing point of the isoimidated solution to a boiling point thereof.
In the step (2), a gelled film in which at least a portion of the polyamic acid has been converted into a polyisoimide is formed. When the gelled film has a percentage of isoimido groups of not lower than 90%, a high stretch ratio is attained advantageously.
It can be said that the first production process has one of its greatest characteristics in that it obtains the unstretched gelled film which is homogeneously and highly swollen and has excellent stretchability in the step (2).
In the step (3), the unstretched gelled film obtained in the step (2) is separated from the substrate and then subjected to biaxial stretching. After separated from the substrate, the unstretched film may be rinsed, or not be rinsed, before subjected to biaxial stretching. To rinse the unstretched film, the same solvents as those used in the above step (1) are used, for example.
The unstretched film can be stretched in longitudinal and transverse directions at a stretch ratio of 1.1 to 6.0. A stretch temperature is not particularly limited and may be any temperature at which stretchability does not deteriorate by the solvent evaporation. For instance, a temperature within a range from xe2x88x9220xc2x0 C. to +80xc2x0 C. is preferred. The unstretched film may be stretched by sequential or simultaneous biaxial stretching, in a solvent, in the air, in an inert atmosphere or in a low temperature heated condition.
The gelled film to be subjected to biaxial stretching in the step (3) preferably has a degree of swelling of 300 to 5,000%. Thereby, a high stretch ratio is attained. When it is lower than 300%, stretchability is not sufficient, while when it is higher than 5,000%, strength of the gel deteriorates, thereby making it difficult to handle the film.
Finally, in the step (4), a biaxially stretched film obtained in the step (3) is subjected to heat treatment so as to form a biaxially oriented polyimide film.
Illustrative examples of a method for heat-treating the film include hot air heating, vacuum heating, infrared heating, microwave heating as well as a method of heating the film by contacting the film with a hot plate or hot roll. During the heat treatment, it is preferred to increase a temperature stepwise so as to promote imidation.
The heat treatment is preferably carried out at 300 to 550xc2x0 C. with the film held at a specific length or under tension. Thereby, relaxation of orientation is suppressed, thereby making it possible to achieve a percentage of imido groups of higher than 95%.
The biaxially stretched film may be rinsed to remove the solvent therefrom before subjected to the heat treatment. To rinse the film, a solvent which can dissolve the solvent such as a lower alcohol, e.g., isopropanol, a higher alcohol, e.g., octyl alcohol, an aromatic hydrocarbon, e.g., toluene and xylene, an ether-based solvent, e.g., dioxane, and a ketone-based solvent, e.g., acetone and methyl ethyl ketone, may be used.
Next, the second production process of the present invention will be described. The second production process comprises the following steps (1) to (4), that is,
(1) preparing a solution of polyamic acid in a solvent, the polyamic acid consisting of a diamine component and a tetracarboxylic acid component, the diamine component comprising p-phenylenediamine whose amount-is more than 80 mol % to 100 mol % and an aromatic diamine component other than p-phenylenediamine whose amount is 0 mol % to less than 20 mol % and the tetracarboxylic acid component comprising pyromellitic acid whose amount is more than 80 mol % and an aromatic tetracarboxylic acid component other than pyromellitic acid whose amount is 0 mol % to less than 20 mol %, the solvent comprising at least one solvent selected from the group consisting of N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and 1,3-dimethylimidazolidinone,
(2) immersing a film obtained by flow casting the solution prepared in the above (1) on a substrate into a solution obtained by dissolving acetic anhydride and an organic amine compound in at least one solvent selected from the above solvents, with the film being attached to the substrate, so as to form a gelled film in which at least a portion of the polyamic acid has been converted into a polyimide or polyisoimide,
(3) separating the obtained gelled film from the substrate, rinsing the film as required, and then biaxially stretching the film, and
(4) subjecting the resulting film to heat treatment, as required, after rinsing the obtained biaxially stretched film to remove the solvent therefrom, so as to form a biaxially oriented polyimide film.
The step (1) is the same as the step (1) in the first production process.
Then, in the step (2), a film obtained by flow casting the solution prepared in the above (1) onto a substrate is immersed into a solution obtained by dissolving acetic anhydride and an organic amine in at least one solvent selected from the same solvents as used in the above step (1), with the film being attached to the substrate.
The organic amine compound used acts as a reaction catalyst for acetic anhydride and polyamic acid. For example, a tertiary aliphatic amine such as trimethylamine, triethylamine, tributylamine, diisopropylethylamine and triethylenediamine; or a heterocyclic compound such as an aromatic amine, e.g., N,N-dimethylaniline and 1,8-bis(N,N-dimethylamino)naphthalene, pyridine and derivatives thereof, picoline and derivatives thereof, lutidine, quinoline, isoquinoline, 1,8-diazabicyclo[5.4.0]undecene and N,N-dimethylaminopyridine can be used. Of these, pyridine and picoline are preferred from the viewpoint of economy. Further, triethylenediamine and N,N-dimethylaminopyridine are also preferably used since they can achieve an extremely high percentage of imido groups and give a gelled film having high water resistance in combination with acetic anhydride. The amount of the organic amine compound based on acetic anhydride is not particularly limited but is not less than 0.5 mol %, preferably not less than 10 mol %.
The concentration of acetic anhydride in the mixed solution is not particularly limited but is preferably 0.5 to 99 wt % so as to cause a reaction to fully proceed. It is more preferably 30 to 99 wt %. A reaction temperature is not particularly limited but may be a temperature within a range from a freezing point of the mixed solution and a boiling point thereof.
It can be said that the second production process has one of its greatest characteristics in that it obtains an unstretched gelled film which is homogeneously and highly swollen and has excellent stretchability by causing acetic anhydride and polyamic acid to react with each other in the presence of an organic amine compound as a catalyst in a solvent which can dissolve the polyamic acid in the step (2).
Subsequently, in the second production process, the step (3) and the step (4) are performed successively. These steps are the same as the steps (3) and (4) in the first production process.
Biaxially oriented polyimide film obtained by the first and second production processes in the manners as described above are a polyimide film with a high Young""s modulus which has molecular chains strongly oriented in a film plane and is excellent in balance in the plane. These films have Young""s moduli measured in two directions perpendicular to each other in the plane of higher than 10 GPa, more preferably 12 GPa, and have improved strength ascribable to a special fine structure formed by stretching and orientation. Such a polyimide film with a high Young""s modulus has high rigidity. Hence, even if the film is a thin film having a thickness of not larger than 10 xcexcm, it can still be suitably used for electronics applications, for example, a substrate for an electric wiring board having a copper foil laminated thereon. Further, it can also be used as substrates for a flexible circuit board, a TAB (Tape Automated Bonding) tape and an LOC (Lead On Chip) tape. In addition, it can also be used as a base film of a magnetic recording tape.